HYDROGEN SORPTION IN ORDERED Mg-In ALLOYS
 Čermák, Jiří ; Král, Lubomír ; Roupcová, Pavla
Hydrogen storage (HS) performance of three Mg- x In- y CB alloys (CB - amorphous carbon, x = 55, 64, 73 y =\n10 wt%) was studied. Indium concentration covered an area of ordered β structures. Alloys were prepared by\nball-milling in hydrogen atmosphere. Kinetic curves and PCT isotherms were measured in the temperature\ninterval from 200 °C to 325 °C. X-ray diffraction spectroscopy (XRD) was used for structure investigation. Alloy\nwith x = 73 wt% In ( β ’’ structure) showed reversible amorphization during temperature cycling between about\n100 °C and 350 °C. Hydrogen sorption experiments were done by the Sieverts method under the hydrogen\ngas pressure ranging from 0.1 MPa to 2.5 MPa. It was found that hydrogen sorption capacity varied between\n0.47 and 1.1 wt% H 2 . Hydride formation enthalpy ∆H calculated from desorption PCT experiments was\nsignificantly lower than ∆H , known for pure Mg. This invoked an idea that atomic order of Mg-based HS\nmaterials might decrease the high thermodynamic stability of hydride phase.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English