Study of biodegradation of poly(hydroxy alkanoates).
Wurstová, Agáta ; Přikryl, Radek (referee) ; Obruča, Stanislav (advisor)
The master‘s thesis is focused on the study of biodegradation of polyhydroxyalkanoates, namely polymer polyhydroxybutyrate. The first part of the thesis is focused on the study of biodegradation of polyhydroxybutyrate in the form of crystalline granules of PHB and PHB films using selected species of microorganisms from bacteria, yeasts and fungi. As a representative of bacteria was chosen microorganism Delftia acidorovans, as yeast was selected Aureobasidium pullulans and Aspergillus fumigatus as fungi. PHB depolymerase activity was measured employing turbidemtiric method with suspension of PHB granules as substrate. The results showed that D. acidorovans can partially degrade PHB. On the contrary A. pullulans cannot effectively degrade PHB. The most significant degradation ability revealed A. fumigatus, which was able to degrade PHB completely. Extracellular enzymes excreted by these microorganisms when cultivated on PHB materials as sole carbon sources were analyzed by SDS-PAGE. The second part of the thesis deals with the biodegradation of PHB in the form of PHB film, PHB hardened foil and PHB Nanoul fabric using standard composting test. Semi-solid cultivation showed positive results. In the interval from 14 days to two months were all forms of the PHB completely biodegraded. With semi-solid cultivation was also studied biodegradation rate of the polyurethane elastomeric films which were modified by partial replacement of polyester polyol by PHB. The test samples were prepared using PHB from Sigma and the PHB samples prepared at the Faculty of chemistry VUT. Samples with different concentrations of the dispersed PHB (1 %, 5 % and 10 %) in the polyurethane were also object of the study. At the end of the cultivation (after 2 months) were measured mechanical properties in tension of the material, then efficiency of biodegradation by gravimetric analysis and modification of the material surface by microscopic analysis.
|
guest ::