Study of cutting defects in flame cutting of limit thickness of carbon steel by fiber laser
Králík, Petr ; Hála, Michal (referee) ; Mrňa, Libor (advisor)
This thesis deals with research of cutting defects at laser cutting of 15 mm thick carbon steel by Bystronic fiber laser with emphasis on wide cutting gap, which causes enlargement of wide of cutting gap and deterioration of roughness of cutting edge and increase of creation fo heat. The introduction describes the main types of lasers used for cutting sheet of metal and compare their advantages and disadvantages. Also described is a cutting process and its parameters, and also the possible cutting defects. An experiment was conducted on steels S355MC and S235JR and cutting defects were analyzed in relation to the set of cutting parameters. Next part determines the extent of the recommended parameters that should be chosen for specific cutting conditions and is balanced recommendations regarding the choice of material to be cut, and technological adaptations parts. In the last part is measured roughness of a wide cutting gap, the width of the heat affected zone and micro-hardness of the material.
|
|
|
Study of cutting defects in flame cutting of limit thickness of carbon steel by fiber laser
Králík, Petr ; Hála, Michal (referee) ; Mrňa, Libor (advisor)
This thesis deals with research of cutting defects at laser cutting of 15 mm thick carbon steel by Bystronic fiber laser with emphasis on wide cutting gap, which causes enlargement of wide of cutting gap and deterioration of roughness of cutting edge and increase of creation fo heat. The introduction describes the main types of lasers used for cutting sheet of metal and compare their advantages and disadvantages. Also described is a cutting process and its parameters, and also the possible cutting defects. An experiment was conducted on steels S355MC and S235JR and cutting defects were analyzed in relation to the set of cutting parameters. Next part determines the extent of the recommended parameters that should be chosen for specific cutting conditions and is balanced recommendations regarding the choice of material to be cut, and technological adaptations parts. In the last part is measured roughness of a wide cutting gap, the width of the heat affected zone and micro-hardness of the material.
|
|
|
Strenght, fracture and fatigue properties of base materials and weld joint of inflow piping to water turbine (PART I - Weld plate to plate)
Dlouhý, Ivo ; Kruml, Tomáš ; Čupera, Pavel ; Chlup, Zdeněk ; Šiška, Filip
Sets of strength, strain, fracture toughness and fatigue properties are summarised in the report characterising the base material, heat affected zones and weld joint material of steel used in water turbine system. Data obtained from 30 mm sheet materials and its weld joint are given. Tests have been carried out in agreement with recent standards and loading curves for finite element calculations have been also supplied. Crack resistance curves have been also generated by unloading technique at 0 and +20°C. Tests of compact tensions in transition regions enabling to determine reference temperature have been carried out. There are also data from fatigue tests, namely cyclic response and fatigue life curves, for the same materials.
|
guest ::