Preparation processes and properties of porous zinc material
Moleková, Kristína ; Březina, Matěj (referee) ; Hasoňová, Michaela (advisor)
Bachelor thesis occupy with preparation of porous material from zinc powder by cold pressing, cold pressing followed by sintering and hot pressing. This thesis contain both preparation of bulk material, and charakterization of materials based on the compaction process conditions. Impact of pressing process on subsequent progress of sintering and final attributes of materials is evaluated. Bulk material is characterized considering to structure, porosity, and physical-mechanical properties. Properties of final metarial will serve to optimize conditions for process of pressing and sintering.
|
|
|
Evolution of pores during sintering of advanced oxide ceramic materials
Spusta, Tomáš ; Kaštyl, Jaroslav (referee) ; Maca, Karel (advisor)
The goal of this bachelor’s thesis is to experimentally specify behaviour of pores in oxide ceramic materials (Al2O3, t-ZrO2, c-ZrO2), particularly to describe the transition from open to close porosity. Ceramics powders made by different producers and with different initial particle size (Al2O3 – AKP30, REYNOLDS, TAIMICRON; ZrO2 + 3 mol.% Y2O3 – TZ3Y, TZ3YSB; ZrO2 + 8 mol.% Y2O3 – TZ8Y, TZ8YSB) were used. Samples were pressed by cold isostatic pressing CIP at pressures of 100MPa and 300MPa, and pressureless sintered up to relative densities up to 88-96%. The obtained results show, that evolution is mainly affected by material, independently of size of initial particles neither by initial shaping pressure. Elimination of open pores occurs in cubic ZrO2 at 91-92 % of relative density, in tetragonal ZrO2 at 92-93 % of relative density and in Al2O3 at 94 % of relative density.
|
|
|
Study of transition from open to closed porosity stage during sintering of advanced ceramic materials
Spusta, Tomáš ; Pouchlý, Václav (referee) ; Maca, Karel (advisor)
Lisovanie za tepla (HIP) je pokročilá technológia pre výrobu plne hutných keramických materiálov, ktoré majú množstvo štruktúrnych (napr. rezné nástroje), biologických (napr. implantáty hutných kostí a kĺbov) alebo funkčných (napr. transparentné štíty a okná) aplikácií. Pre úspešné použitie tejto technológie je potrebné, aby predspekané vzorky boli plynotesné, teda bez otvorených pórov. Výskum zaoberajúci sa premenou otvorených pórov na uzatvorené je preto veľmi dôležitý, avšak iba málo publikovaný v odbornej literatúre. Preto bolo experimentálne a teoretické štúdium tohto javu hlavným cieľom diplomovej práce. Analýzy teoretických modelov ukazujú, že transformácia z otvorenej na uzatvorenú pórovitosť je materiálová charakteristika, ktoré sa mení iba s dihedrálnym uhlom, nezávisle na veľkosti častíc prášku alebo na spôsobe tvarovania a nastáva od 92.6% t.d. do 93.7% t.d pre daný materiál (oxid hlinitý, oxid zirkoničitý a horečnato-hlinitý spinel). Tieto teoretické výpočty boli porovnané s experimentálnymi dátami z literatúry a dátami z experimentálnej časti diplomovej práce s úspešnou zhodou pre kubické systémy (spinel a kubický oxid zirkoničitý). Výsledky experimentov s oxidom hlinitým boli v dobrej zhode s experimentálnymi dátami publikovanými v literatúre, ale boli vyššie ako teoretické hodnoty. Na objasnenie týchto odlišností bolo vytvorených niekoľko hypotéz a tiež boli navrhnuté spôsoby riešenia tejto témy.
|
|
|
Preparation processes and properties of porous zinc material
Moleková, Kristína ; Březina, Matěj (referee) ; Hasoňová, Michaela (advisor)
Bachelor thesis occupy with preparation of porous material from zinc powder by cold pressing, cold pressing followed by sintering and hot pressing. This thesis contain both preparation of bulk material, and charakterization of materials based on the compaction process conditions. Impact of pressing process on subsequent progress of sintering and final attributes of materials is evaluated. Bulk material is characterized considering to structure, porosity, and physical-mechanical properties. Properties of final metarial will serve to optimize conditions for process of pressing and sintering.
|
|
|
Study of transition from open to closed porosity stage during sintering of advanced ceramic materials
Spusta, Tomáš ; Pouchlý, Václav (referee) ; Maca, Karel (advisor)
Lisovanie za tepla (HIP) je pokročilá technológia pre výrobu plne hutných keramických materiálov, ktoré majú množstvo štruktúrnych (napr. rezné nástroje), biologických (napr. implantáty hutných kostí a kĺbov) alebo funkčných (napr. transparentné štíty a okná) aplikácií. Pre úspešné použitie tejto technológie je potrebné, aby predspekané vzorky boli plynotesné, teda bez otvorených pórov. Výskum zaoberajúci sa premenou otvorených pórov na uzatvorené je preto veľmi dôležitý, avšak iba málo publikovaný v odbornej literatúre. Preto bolo experimentálne a teoretické štúdium tohto javu hlavným cieľom diplomovej práce. Analýzy teoretických modelov ukazujú, že transformácia z otvorenej na uzatvorenú pórovitosť je materiálová charakteristika, ktoré sa mení iba s dihedrálnym uhlom, nezávisle na veľkosti častíc prášku alebo na spôsobe tvarovania a nastáva od 92.6% t.d. do 93.7% t.d pre daný materiál (oxid hlinitý, oxid zirkoničitý a horečnato-hlinitý spinel). Tieto teoretické výpočty boli porovnané s experimentálnymi dátami z literatúry a dátami z experimentálnej časti diplomovej práce s úspešnou zhodou pre kubické systémy (spinel a kubický oxid zirkoničitý). Výsledky experimentov s oxidom hlinitým boli v dobrej zhode s experimentálnymi dátami publikovanými v literatúre, ale boli vyššie ako teoretické hodnoty. Na objasnenie týchto odlišností bolo vytvorených niekoľko hypotéz a tiež boli navrhnuté spôsoby riešenia tejto témy.
|
|
|
Evolution of pores during sintering of advanced oxide ceramic materials
Spusta, Tomáš ; Kaštyl, Jaroslav (referee) ; Maca, Karel (advisor)
The goal of this bachelor’s thesis is to experimentally specify behaviour of pores in oxide ceramic materials (Al2O3, t-ZrO2, c-ZrO2), particularly to describe the transition from open to close porosity. Ceramics powders made by different producers and with different initial particle size (Al2O3 – AKP30, REYNOLDS, TAIMICRON; ZrO2 + 3 mol.% Y2O3 – TZ3Y, TZ3YSB; ZrO2 + 8 mol.% Y2O3 – TZ8Y, TZ8YSB) were used. Samples were pressed by cold isostatic pressing CIP at pressures of 100MPa and 300MPa, and pressureless sintered up to relative densities up to 88-96%. The obtained results show, that evolution is mainly affected by material, independently of size of initial particles neither by initial shaping pressure. Elimination of open pores occurs in cubic ZrO2 at 91-92 % of relative density, in tetragonal ZrO2 at 92-93 % of relative density and in Al2O3 at 94 % of relative density.
|