Fracture tests of selected specimens with special aggregates: experiments and numerical simulation
Majda, Tomáš ; Malíková, Lucie (referee) ; Keršner, Zbyněk (advisor)
The diploma thesis deals with selected fracture tests and evaluation of fracture parameters of cement-based composite. One part of the thesis deals with cement-based composite with glass spherical aggregate of a single fraction of 2 mm. After production, the beams with dimensions of 20×40×200mm exposed to temperatures in the range from 100 to 1000 °C for one hour. Using the non-destructive ultrasonic pulse method, the degree of damage caused by termal load was determined. Selected specimen with central edge notch were then tested in three-point bending and fragments after these tests were tested in compression. In the second part, attention was paid to the evaluation of fracture tests conducted on specimen from drill-cores taken from selected objects located at the former Transgas Gas Control Center in Prague. The specimen were provided with a chevron notch before being tested in three-point bending. The measured data was modified by the GTDiPS program and in the case of the glass composite the StiCrack program was used to evaluate fracture parameters.
|
|
|
Advanced evaluation of fracture tests of selected rock specimens
Kubeš, Pavel ; Veselý, Václav (referee) ; Keršner, Zbyněk (advisor)
This bachelor's thesis deals with the advanced evaluation of fracture tests of selected rock (sandstone) specimens. The first part describes several fracture models/methods, fracture-mechanical parameters, process and configuration of the tests, used specimens and the procedure of data processing using the program GTDiPS. The second part contains neatly sorted evaluation of load-displacement diagrams. The results of the work are calculated fracture-mechanical parameters of various sandstones and their mutual comparison.
|
|
|
Advanced evaluation of selected fracture tests of fibre reinforcement concrete specimens
Majda, Tomáš ; Frantík, Petr (referee) ; Keršner, Zbyněk (advisor)
The goal of this thesis was evaluation of extensive series of selected three point bending tests on fibre reinforced concrete specimens of ages 7, 28 and 126 days. First the measured data were adjusted by GTDiPS software. Than the assumed contribution of fibres in load--deflection diagram was approximated by regressive function. Contribution of matrix was calculated by deducting the approximated part from full diagram. Using StiCrack software the Young modulus, fracture toughness and fracture energy were calculated for both original and approximated diagram. All results were evaluated and tabled.
|
|
|
Evaluation and simulations of fracture test of concrete specimens in selected configurations
Halfar, Petr ; Šimonová, Hana (referee) ; Keršner, Zbyněk (advisor)
This thesis deals with the evaluation of the selected fracture test configurations of concrete specimens. These configurations are the wedge splitting test or combinations of wedge splitting test and three point bending. The first part is theoretical and it describes the use of fracture mechanics on the quasi-brittle material - concrete. There are also described linear and nonlinear fracture theory, improvement process of fracture tests and also determination of the fracture parameters from the tests. The second part is practical and it describes editing of load-displacement diagrams by using GTDiPS application and then evaluation of the diagrams. The result of this work is comparison of the concrete fracture energy in each geometric variations of the tests.
|
|
|
Fracture tests of selected specimens with special aggregates: experiments and numerical simulation
Majda, Tomáš ; Malíková, Lucie (referee) ; Keršner, Zbyněk (advisor)
The diploma thesis deals with selected fracture tests and evaluation of fracture parameters of cement-based composite. One part of the thesis deals with cement-based composite with glass spherical aggregate of a single fraction of 2 mm. After production, the beams with dimensions of 20×40×200mm exposed to temperatures in the range from 100 to 1000 °C for one hour. Using the non-destructive ultrasonic pulse method, the degree of damage caused by termal load was determined. Selected specimen with central edge notch were then tested in three-point bending and fragments after these tests were tested in compression. In the second part, attention was paid to the evaluation of fracture tests conducted on specimen from drill-cores taken from selected objects located at the former Transgas Gas Control Center in Prague. The specimen were provided with a chevron notch before being tested in three-point bending. The measured data was modified by the GTDiPS program and in the case of the glass composite the StiCrack program was used to evaluate fracture parameters.
|
|
|
Advanced evaluation of selected fracture tests of fibre reinforcement concrete specimens
Majda, Tomáš ; Frantík, Petr (referee) ; Keršner, Zbyněk (advisor)
The goal of this thesis was evaluation of extensive series of selected three point bending tests on fibre reinforced concrete specimens of ages 7, 28 and 126 days. First the measured data were adjusted by GTDiPS software. Than the assumed contribution of fibres in load--deflection diagram was approximated by regressive function. Contribution of matrix was calculated by deducting the approximated part from full diagram. Using StiCrack software the Young modulus, fracture toughness and fracture energy were calculated for both original and approximated diagram. All results were evaluated and tabled.
|
|
|
Evaluation and simulations of fracture test of concrete specimens in selected configurations
Halfar, Petr ; Šimonová, Hana (referee) ; Keršner, Zbyněk (advisor)
This thesis deals with the evaluation of the selected fracture test configurations of concrete specimens. These configurations are the wedge splitting test or combinations of wedge splitting test and three point bending. The first part is theoretical and it describes the use of fracture mechanics on the quasi-brittle material - concrete. There are also described linear and nonlinear fracture theory, improvement process of fracture tests and also determination of the fracture parameters from the tests. The second part is practical and it describes editing of load-displacement diagrams by using GTDiPS application and then evaluation of the diagrams. The result of this work is comparison of the concrete fracture energy in each geometric variations of the tests.
|
|
|
Advanced evaluation of fracture tests of selected rock specimens
Kubeš, Pavel ; Veselý, Václav (referee) ; Keršner, Zbyněk (advisor)
This bachelor's thesis deals with the advanced evaluation of fracture tests of selected rock (sandstone) specimens. The first part describes several fracture models/methods, fracture-mechanical parameters, process and configuration of the tests, used specimens and the procedure of data processing using the program GTDiPS. The second part contains neatly sorted evaluation of load-displacement diagrams. The results of the work are calculated fracture-mechanical parameters of various sandstones and their mutual comparison.
|