Evaluation of electrochemical characteristics of AZ61 magnesium alloy processed by squeeze casting
Pikner, Jan ; Hadzima, Branislav (referee) ; Fintová, Stanislava (advisor)
Bachelor thesis deals with the characterization of electrochemical corrosion properties of AZ61 magnesium alloy prepared by squeeze casting method. The theoretical part of the work focuses on properties of AZ61 alloy, influence of alloying elements on magnesium alloys and corrosion. The practical part of the work deals with electrochemical characteristics of AZ61 alloy with different surface condition in of 0.1 M NaCl solution. Corrosion potential (Ekor) and corrosion current density (ikor) were determined by potentiodynamic test. Polarisation resistance was determined by electrochemical impedance spectroscopy. Based on the measured results was discussed the influence of production, chemical composition, structure and surface treatment (grinding and polishing) on corrosion characteristics of the alloy.
|
|
|
Evaluation of electrochemical properties of wrought Mg-Al-Zn type magnesium alloys
Slouková, Karolína ; Hadzima, Branislav (referee) ; Tkacz, Jakub (advisor)
The aim of this master’s thesis is electrochemical characteristics evaluation of magnesium alloys. The theoretical part describes the properties of magnesium and its alloys and their corrosion characteristics. In the experimental part are presented results of corrosion resistance measurement of two types of wrought magnesium alloys. It was AZ31 and AZ61 magnesium alloys, which were measured in Hank’s solutions with addition of ions Ca2+ and Mg2+ (SBF+) and without addition of the ions (SBF). The solution temperature during the measurement was 37 ± 1 °C. The experiments were used electrochemical impedance spectroscopy (EIS) and potentiodynamic tests using linear polarization (LP). EIS measurements were done in times of 5 minutes, 1, 2, 4, 8, 12, 24, 48, 72, 96 and 168 hours. Potentiodynamic tests were only short-term and they started after 5 minutes of stabilization. Both methods were used for measuring the electrochemical characteristics of polished and ground surface of the samples. The most important measurement results were polarization resistance, corrosion potential and corrosion current density. The electrochemical measurements are used to estimate the chemical composition influence and alloy’s structure of the corrosion resistance.
|
|
|
Evaluation of electrochemical characteristics of AZ61 magnesium alloy processed by squeeze casting
Pikner, Jan ; Hadzima, Branislav (referee) ; Fintová, Stanislava (advisor)
Bachelor thesis deals with the characterization of electrochemical corrosion properties of AZ61 magnesium alloy prepared by squeeze casting method. The theoretical part of the work focuses on properties of AZ61 alloy, influence of alloying elements on magnesium alloys and corrosion. The practical part of the work deals with electrochemical characteristics of AZ61 alloy with different surface condition in of 0.1 M NaCl solution. Corrosion potential (Ekor) and corrosion current density (ikor) were determined by potentiodynamic test. Polarisation resistance was determined by electrochemical impedance spectroscopy. Based on the measured results was discussed the influence of production, chemical composition, structure and surface treatment (grinding and polishing) on corrosion characteristics of the alloy.
|
|
|
Evaluation of electrochemical properties of AZ31 magnesium alloy prepared by sqeeze casting
Mikulášová, Kristýna ; Drábiková, Juliána (referee) ; Tkacz, Jakub (advisor)
The bachelor thesis deals with electrochemical characterization of corrosion properties of magnesium alloy AZ31. This alloy produced by squeeze casting method was exposed to a corrosive environment of 0,1 M solution of NaCl. Scanning electron microscopy (SEM) with elemental analysis measured by energy dispersive spectroscopy (EDS) was used for the evaluation of the AZ31 magnesium alloy’s surface. Consequently, short term corrosion tests (5 min) were undertaken by potentiodynamic tests. Long term tests (168 h) were measured by electrochemical impedance spectroscopy (EIS). The effects of different alloy surface treatment (grinding and polishing) on the corrosion rate of the AZ31 magnesium alloy produced by squeeze casting method were evaluated by measured results.
|
|
|
Evaluation of electrochemical properties of wrought Mg-Al-Zn type magnesium alloys
Slouková, Karolína ; Hadzima, Branislav (referee) ; Tkacz, Jakub (advisor)
The aim of this master’s thesis is electrochemical characteristics evaluation of magnesium alloys. The theoretical part describes the properties of magnesium and its alloys and their corrosion characteristics. In the experimental part are presented results of corrosion resistance measurement of two types of wrought magnesium alloys. It was AZ31 and AZ61 magnesium alloys, which were measured in Hank’s solutions with addition of ions Ca2+ and Mg2+ (SBF+) and without addition of the ions (SBF). The solution temperature during the measurement was 37 ± 1 °C. The experiments were used electrochemical impedance spectroscopy (EIS) and potentiodynamic tests using linear polarization (LP). EIS measurements were done in times of 5 minutes, 1, 2, 4, 8, 12, 24, 48, 72, 96 and 168 hours. Potentiodynamic tests were only short-term and they started after 5 minutes of stabilization. Both methods were used for measuring the electrochemical characteristics of polished and ground surface of the samples. The most important measurement results were polarization resistance, corrosion potential and corrosion current density. The electrochemical measurements are used to estimate the chemical composition influence and alloy’s structure of the corrosion resistance.
|