Reasons for pin holes formation in ductile iron castings
Opačitý, Radim ; Palán, Petr (referee) ; Šenberger, Jaroslav (advisor)
The aim of this thesis was to analyze the formation of defects in a given casting of ductile cast iron EN - GJS - 600-3 cast in sand molds bentonite, which is formed jolting with coining and then find a solution to remedy these defects. To resolve this issue, the influence of the composition of the sand mixture, the effect of metal flow in a cavity forms and the influence of deoxidation of metal in the presence of defects. Obtained results showed the importance of the influence Reoxidation metal cavity mold. Specifically, in this case succeeded in reducing the incidence of PINHOLES. Removal of PINHOLES to achieve deoxidation aluminum melt. This has reduced the production of nonconforming castings under 3% from the original 6.5%.
|
|
|
Manufacturing and defects of steel castings
Smilovský, David ; Čamek, Libor (referee) ; Záděra, Antonín (advisor)
A content of this thesis is an analysis of a steel castings production mismatch in Tatra Metallurgy foundry. Most common defects found on castings are gas holes. Thesis shows a theoretical research on casting defects caused by gases in steel castings. It also describes melting and degassing problematics of molten steel and procedures to reduce gas contents. The last part of theoretical research describes oxidation of steel in contact with silica mold. Practical part of thesis analysis production of steel castings to determine the cause of origin of gas holes. Main attention is paid to mold mixture, chemical composition, casting temperatures and casting time. The last chapter metallographically analysis two defected castings to determine the origin of defects. Main attention is paid to shape and chemical composition of gas holes and to morphology of steel inclusions.
|
|
|
Manufacturing and defects of steel castings
Smilovský, David ; Čamek, Libor (referee) ; Záděra, Antonín (advisor)
A content of this thesis is an analysis of a steel castings production mismatch in Tatra Metallurgy foundry. Most common defects found on castings are gas holes. Thesis shows a theoretical research on casting defects caused by gases in steel castings. It also describes melting and degassing problematics of molten steel and procedures to reduce gas contents. The last part of theoretical research describes oxidation of steel in contact with silica mold. Practical part of thesis analysis production of steel castings to determine the cause of origin of gas holes. Main attention is paid to mold mixture, chemical composition, casting temperatures and casting time. The last chapter metallographically analysis two defected castings to determine the origin of defects. Main attention is paid to shape and chemical composition of gas holes and to morphology of steel inclusions.
|
|
|
Reasons for pin holes formation in ductile iron castings
Opačitý, Radim ; Palán, Petr (referee) ; Šenberger, Jaroslav (advisor)
The aim of this thesis was to analyze the formation of defects in a given casting of ductile cast iron EN - GJS - 600-3 cast in sand molds bentonite, which is formed jolting with coining and then find a solution to remedy these defects. To resolve this issue, the influence of the composition of the sand mixture, the effect of metal flow in a cavity forms and the influence of deoxidation of metal in the presence of defects. Obtained results showed the importance of the influence Reoxidation metal cavity mold. Specifically, in this case succeeded in reducing the incidence of PINHOLES. Removal of PINHOLES to achieve deoxidation aluminum melt. This has reduced the production of nonconforming castings under 3% from the original 6.5%.
|