RESIDUAL FATIGUE LIFETIME OF RAILWAY AXLES
Pokorný, Pavel ; Fajkoš,, Rostislav (referee) ; Materna, Aleš (referee) ; Náhlík, Luboš (advisor)
This Ph.D. thesis deals with methodology for determination of residual fatigue lifetime of railway axles based on damage tolerance approach. This approach accepts an existence of potential defect, which could lead to fatigue failure of whole axle. The behavior of crack in railway axle is described by approaches of linear elastic fracture mechanics. There are plenty of factors, which more or less influence determined residual fatigue lifetime. The aim of this thesis is to quantify effects of these factors. The first part of Ph.D. thesis represents overview of studied problems relating to fatigue damage of railway axles. This part is focused on parameters, which influence fatigue crack growth in railway axle materials. The second part of thesis shows procedure for determination of residual fatigue lifetime, which was developed at the Institute of Physics of Materials of the Academy of Sciences of the Czech Republic. The main aim of this thesis was to improve current procedure for more precise estimation of residual fatigue lifetime. Significant part of this work is determination of significance of studied factors, which influencing calculated residual fatigue lifetime of railway axles (e.g. effect of threshold value, load spectrum, retardation effects, residual stress, axle geometry, material of axle etc.). The procedures described and results obtained can be also used for determination of residual fatigue lifetime of general mechanical component (not only railway axles). Therefore, results obtained in this Ph.D. thesis can be used e.g. for assessment of regular inspection intervals of cyclically loaded general mechanical parts.
|
|
|
RESIDUAL FATIGUE LIFETIME OF RAILWAY AXLES
Pokorný, Pavel ; Fajkoš,, Rostislav (referee) ; Materna, Aleš (referee) ; Náhlík, Luboš (advisor)
This Ph.D. thesis deals with methodology for determination of residual fatigue lifetime of railway axles based on damage tolerance approach. This approach accepts an existence of potential defect, which could lead to fatigue failure of whole axle. The behavior of crack in railway axle is described by approaches of linear elastic fracture mechanics. There are plenty of factors, which more or less influence determined residual fatigue lifetime. The aim of this thesis is to quantify effects of these factors. The first part of Ph.D. thesis represents overview of studied problems relating to fatigue damage of railway axles. This part is focused on parameters, which influence fatigue crack growth in railway axle materials. The second part of thesis shows procedure for determination of residual fatigue lifetime, which was developed at the Institute of Physics of Materials of the Academy of Sciences of the Czech Republic. The main aim of this thesis was to improve current procedure for more precise estimation of residual fatigue lifetime. Significant part of this work is determination of significance of studied factors, which influencing calculated residual fatigue lifetime of railway axles (e.g. effect of threshold value, load spectrum, retardation effects, residual stress, axle geometry, material of axle etc.). The procedures described and results obtained can be also used for determination of residual fatigue lifetime of general mechanical component (not only railway axles). Therefore, results obtained in this Ph.D. thesis can be used e.g. for assessment of regular inspection intervals of cyclically loaded general mechanical parts.
|
|
|
RESIDUAL FATIGUE LIFETIME OF RAILWAY AXLES
Pokorný, Pavel ; Fajkoš,, Rostislav (referee) ; Materna, Aleš (referee) ; Náhlík, Luboš (advisor)
This Ph.D. thesis deals with methodology for determination of residual fatigue lifetime of railway axles based on damage tolerance approach. This approach accepts an existence of potential defect, which could lead to fatigue failure of whole axle. The behavior of crack in railway axle is described by approaches of linear elastic fracture mechanics. There are plenty of factors, which more or less influence determined residual fatigue lifetime. The aim of this thesis is to quantify effects of these factors. The first part of Ph.D. thesis represents overview of studied problems relating to fatigue damage of railway axles. This part is focused on parameters, which influence fatigue crack growth in railway axle materials. The second part of thesis shows procedure for determination of residual fatigue lifetime, which was developed at the Institute of Physics of Materials of the Academy of Sciences of the Czech Republic. The main aim of this thesis was to improve current procedure for more precise estimation of residual fatigue lifetime. Significant part of this work is determination of significance of studied factors, which influencing calculated residual fatigue lifetime of railway axles (e.g. effect of threshold value, load spectrum, retardation effects, residual stress, axle geometry, material of axle etc.). The procedures described and results obtained can be also used for determination of residual fatigue lifetime of general mechanical component (not only railway axles). Therefore, results obtained in this Ph.D. thesis can be used e.g. for assessment of regular inspection intervals of cyclically loaded general mechanical parts.
|
|
|
RESIDUAL FATIGUE LIFETIME OF RAILWAY AXLES
Pokorný, Pavel ; Fajkoš,, Rostislav (referee) ; Materna, Aleš (referee) ; Náhlík, Luboš (advisor)
This Ph.D. thesis deals with methodology for determination of residual fatigue lifetime of railway axles based on damage tolerance approach. This approach accepts an existence of potential defect, which could lead to fatigue failure of whole axle. The behavior of crack in railway axle is described by approaches of linear elastic fracture mechanics. There are plenty of factors, which more or less influence determined residual fatigue lifetime. The aim of this thesis is to quantify effects of these factors. The first part of Ph.D. thesis represents overview of studied problems relating to fatigue damage of railway axles. This part is focused on parameters, which influence fatigue crack growth in railway axle materials. The second part of thesis shows procedure for determination of residual fatigue lifetime, which was developed at the Institute of Physics of Materials of the Academy of Sciences of the Czech Republic. The main aim of this thesis was to improve current procedure for more precise estimation of residual fatigue lifetime. Significant part of this work is determination of significance of studied factors, which influencing calculated residual fatigue lifetime of railway axles (e.g. effect of threshold value, load spectrum, retardation effects, residual stress, axle geometry, material of axle etc.). The procedures described and results obtained can be also used for determination of residual fatigue lifetime of general mechanical component (not only railway axles). Therefore, results obtained in this Ph.D. thesis can be used e.g. for assessment of regular inspection intervals of cyclically loaded general mechanical parts.
|