The specimen size effect on R-curve and on crack tip blunting
Mrňa, Tomáš ; Konopík,, Pavel (referee) ; Stratil, Luděk (advisor)
The thesis deals with the determination of fracture toughness using compact tension (CT) test specimens at elevated and high temperatures. The experimental material steel P91 designated for application at temperatures 550650°C was used. The fracture toughness in the ductile fracture region of the steel was characterized by the R curve, which characterises the resistance against crack propagation depending on the crack length. The effect of temperature on the R curve at range 23600°C was evaluated. Next the specimen size effect using three sizes of CT specimens at 23°C and the effect of loading rate (2, 0,2 a 0,02 mm/min) at 600°C was examined. The results showed that the temperature has distinct effect on the R-curve, which yields minimal values at 400°C. Only the smallest test specimen size with thickness 6.25mm showed the specimen size effect giving about 10% lower values of toughness comparing to larger specimens. The effect of loading rate was clearly distinguishable. The values of toughness varied about 20% of the toughness value comparing individual loading rate.
|
|
|
Fracture toughness testing at high temperature range using miniaturized CT specimens
Lokvenc, Martin ; Chlup, Zdeněk (referee) ; Stratil, Luděk (advisor)
This thesis deals with a high temperature testing of fracture toughness and studies the size effect on measured values using miniature size CT specimen. Two types of specimen geometry were manufactured from P91 steel, the standard size and the quarter size specimen. J-R curves were obtained in the temperature range from 23°C to 600°C. No specimen size effect was observed at room temperature tests. The realized experiments together with fractography analysis demonstrated the drop of toughness at 400°C caused by the effect of dynamic strain aging.
|
|
|
The specimen size effect on R-curve and on crack tip blunting
Mrňa, Tomáš ; Konopík,, Pavel (referee) ; Stratil, Luděk (advisor)
The thesis deals with the determination of fracture toughness using compact tension (CT) test specimens at elevated and high temperatures. The experimental material steel P91 designated for application at temperatures 550650°C was used. The fracture toughness in the ductile fracture region of the steel was characterized by the R curve, which characterises the resistance against crack propagation depending on the crack length. The effect of temperature on the R curve at range 23600°C was evaluated. Next the specimen size effect using three sizes of CT specimens at 23°C and the effect of loading rate (2, 0,2 a 0,02 mm/min) at 600°C was examined. The results showed that the temperature has distinct effect on the R-curve, which yields minimal values at 400°C. Only the smallest test specimen size with thickness 6.25mm showed the specimen size effect giving about 10% lower values of toughness comparing to larger specimens. The effect of loading rate was clearly distinguishable. The values of toughness varied about 20% of the toughness value comparing individual loading rate.
|
|
|
Fracture toughness testing at high temperature range using miniaturized CT specimens
Lokvenc, Martin ; Chlup, Zdeněk (referee) ; Stratil, Luděk (advisor)
This thesis deals with a high temperature testing of fracture toughness and studies the size effect on measured values using miniature size CT specimen. Two types of specimen geometry were manufactured from P91 steel, the standard size and the quarter size specimen. J-R curves were obtained in the temperature range from 23°C to 600°C. No specimen size effect was observed at room temperature tests. The realized experiments together with fractography analysis demonstrated the drop of toughness at 400°C caused by the effect of dynamic strain aging.
|