Glass-ceramic composite biomaterials
 Žaludek, Jakub ; Hadraba, Hynek (referee) ; Drdlík, Daniel (advisor)
The bachelor thesis is focused on the preparation of bioglass 45S5 and composites containing bioglass 45S5 and alumina or zirconia fibres in amount of 1, 3 and 5 wt% by slip-casting method from aqueous and 2-propanolic suspensions. The materials prepared were characterised in term their porosity, relative density, high temperature dilatometry, X-ray diffraction analysis, microstructure and hardness. The slip-casting method produced porous samples which is promising result for a possible biomedical application. The high temperature dilatometry identified three stages of the sintering process and a shrinkage of ~40% of the bioglass-based materials was measured. The crystalline phase of Na2Ca2Si3O9 was created at the sintering temperature of 1050°C but the dissolution of Al2O3 or ZrO2 fibres into the bioglass matrix was not confirmed using the X-ray diffraction analysis. It was found that the hardness of the samples decreased with the amount of the fibres in the materials which was caused by their increasing porosity and large clusters of fibres.
Detailed record
Glass-ceramic composite biomaterials
 Žaludek, Jakub ; Hadraba, Hynek (referee) ; Drdlík, Daniel (advisor)
The bachelor thesis is focused on the preparation of bioglass 45S5 and composites containing bioglass 45S5 and alumina or zirconia fibres in amount of 1, 3 and 5 wt% by slip-casting method from aqueous and 2-propanolic suspensions. The materials prepared were characterised in term their porosity, relative density, high temperature dilatometry, X-ray diffraction analysis, microstructure and hardness. The slip-casting method produced porous samples which is promising result for a possible biomedical application. The high temperature dilatometry identified three stages of the sintering process and a shrinkage of ~40% of the bioglass-based materials was measured. The crystalline phase of Na2Ca2Si3O9 was created at the sintering temperature of 1050°C but the dissolution of Al2O3 or ZrO2 fibres into the bioglass matrix was not confirmed using the X-ray diffraction analysis. It was found that the hardness of the samples decreased with the amount of the fibres in the materials which was caused by their increasing porosity and large clusters of fibres.
Detailed record

Interested in being notified about new results for this query?
Subscribe to the RSS feed.
Digital Repository :: Search :: Submit :: Personalize :: Help
Powered by Invenio v1.1.2
Maintained by admin.invenio@techlib.cz
This site is also available in the following languages:
Česky  English