HYDROGENATION PROPERTIES OF Mg-Al-Ti-Zr-C COMPOSITE
Král, Lubomír ; Čermák, Jiří ; Roupcová, Pavla
The improvement of hydrogen storage properties of ball-milled Mg-Al-Ti-Zr-C composite was studied in this\npaper. It has been previously shown, that the addition of Ti, Zr, Al and C improves storage properties of Mg.\nThis beneficial effect of additives upon hydrogen storage properties can be explained by catalysis by the\nnanoparticles rich in Ti, Zr or Al located on the surface of Mg grains. They provide effective pathways for the\nhydrogen diffusion into the MgH2. The morphological and microstructural characteristics were investigated by\nscanning electron microscope Tescan Lyra 3 and by X-ray diffraction. The hydrogen sorption was measured\nby Sieverts method using Setaram PCT-Pro device.\nStudied experimental composite absorbed 4.2 wt.% H 2 at 573 K and 3 wt.% H 2 at 523K within 10 min. The\nhydrogen storage capacity of the composite was about 4.6% wt.% H 2 and 4.2% wt.% H 2 at 573K and 523K,\nrespectively.
|
|
|
HYDROGEN ABSORPTION IN A-Co30Fe55B15
Čermák, Jiří ; Král, Lubomír ; Roupcová, Pavla
Hydrogen solved in amorphous alloys (AAs) influences their magnetic characteristics. AAs are also perspective\nas additives that can improve hydrogen storage kinetic in certain types of ball-milled hydrogen storage\nmaterials (HSMs). Therefore, knowledge of hydrogen solubility and hydrogen sorption kinetics in AAs are of a\ngreat importance for aimed design both AAs with optimal magnetic parameters and HSMs with desired sorption\ncharacteristics. In the present paper, amorphous alloy Co30Fe55B15 (an example of the type a-TM1xTM2y Bz ;\nTM - transition metal) was investigated. Hydrogen concentration c H was measured by Sieverts method in\ntemperature interval from T = 150 °C to T = 350 °C under hydrogen pressure p up to 6 MPa. It was found that\nc H was an increasing function of p and its maximum value was typically 0.5 wt.% H2 at 350 °C and 6 MPa.\nHowever, when the alloy was preliminary hydrogen charged (PHC), the pressure dependence of total c Htot in\nthe first absorption cycle(s) is non-monotonous in dependence on PHC conditions. For the sake of comparison,\nthe same absorption characteristics were measured also in Mg2Ni intermetallic that is a common constituent\nin Mg-based HSMs. Comparing Co30Fe55B15 and Mg2Ni, it was concluded that Co30Fe55B15 shows lower\nhydrogen solubility, but much better absorption kinetics.
|
guest ::