Ceramic dental restoration milling from stock based on ZrO2
Ščasnovič, Erik ; Spusta, Tomáš (referee) ; Kaštyl, Jaroslav (advisor)
In this bachelor thesis, the theoretical overview about the milling of the dental zirconia blanks was performed. The tests of biaxial flexural strength were evaluated in the experimental part, as well as the roughness and the grain size in sintered state and the linear shrinkage was determined. These tests were done for gel cast blanks from zirconia dioxide prepared in laboratories and also for two types of commercially available zirconia oxide blanks fabricated by cold isostatic pressing. The relationship between strength and grain size was shown. The samples prepared from gel cast blanks had statistically significantly higher strength than samples from commercial blanks. At the end of the thesis, the milling of dental crown was carried out based on real tooth model from gel cast zirconia blank studied in this thesis.
|
|
|
Milling of pre-sintered ceramics using CAD / CAM
Ščasnovič, Erik ; Pouchlý, Václav (referee) ; Kaštyl, Jaroslav (advisor)
Diploma thesis is focused on determination of proper pre-sintering temperatures of zirconia ceramic blanks intended for CAD-CAM milling. Functional properties of milled and sintered samples are also discussed. Experimental part is aimed on determination of properties of blanks which affect directly the CAD-CAM process. Another solved issue is definition of mechanical and physical properties of sintered bodies. Final properties are compared with properties of ceramic blanks made from standard ceramic powder. Dental crown, dental three-unit bridge and partial knee joint were prepared successfully. The tests of geometric accuracy were performed on dental crown as well as on partial knee joint replacement with using 3D scanner.
|
|
|
Milling of pre-sintered ceramics using CAD / CAM
Ščasnovič, Erik ; Pouchlý, Václav (referee) ; Kaštyl, Jaroslav (advisor)
Diploma thesis is focused on determination of proper pre-sintering temperatures of zirconia ceramic blanks intended for CAD-CAM milling. Functional properties of milled and sintered samples are also discussed. Experimental part is aimed on determination of properties of blanks which affect directly the CAD-CAM process. Another solved issue is definition of mechanical and physical properties of sintered bodies. Final properties are compared with properties of ceramic blanks made from standard ceramic powder. Dental crown, dental three-unit bridge and partial knee joint were prepared successfully. The tests of geometric accuracy were performed on dental crown as well as on partial knee joint replacement with using 3D scanner.
|
|
|
Ceramic dental restoration milling from stock based on ZrO2
Ščasnovič, Erik ; Spusta, Tomáš (referee) ; Kaštyl, Jaroslav (advisor)
In this bachelor thesis, the theoretical overview about the milling of the dental zirconia blanks was performed. The tests of biaxial flexural strength were evaluated in the experimental part, as well as the roughness and the grain size in sintered state and the linear shrinkage was determined. These tests were done for gel cast blanks from zirconia dioxide prepared in laboratories and also for two types of commercially available zirconia oxide blanks fabricated by cold isostatic pressing. The relationship between strength and grain size was shown. The samples prepared from gel cast blanks had statistically significantly higher strength than samples from commercial blanks. At the end of the thesis, the milling of dental crown was carried out based on real tooth model from gel cast zirconia blank studied in this thesis.
|