Experimental study of friction in articular cartilage
Praus, Tomáš ; Vrbka, Martin (referee) ; Rebenda, David (advisor)
This thesis deals with the experimental study of friction in articular cartilage. After the introduction to biotribology, there are described a principle of measurment on the Mini-Traction Machine and a brief description of machine itself. After that, there is a propose for a preparation and storage of cartilage samples, construction of the adapter into the MTM and research of the friction coefficient. The results of experimental research showed the negative effect of storing the samples in the refrigerator. On the other hand, the measurement of the friction coefficient of the samples stored in the freezer showed the preservation of the mechanical properties of cartilage. Even load and speed of loading have a big effect on friction. When the speed increases, the coefficient of the friction increases too. There is an extreme increase of the friction at higher speeds. But with increasing load the friction coefficient decreases.
|
|
|
The Effect of Synovial Fluid Constituents on Lubrication of Hip Joint Replacements
Nečas, David ; Daniel,, Matej (referee) ; Sawae, Yoshinori (referee) ; Hartl, Martin (advisor)
Dizertační práce se zabývá mechanismy mazání v náhradách kyčelního kloubu. Byla provedena systematická studie formování proteinového filmu při zahrnutí různých materiálů a provozních podmínek. Hlavní pozornost je přitom věnována roli jednotlivých proteinů obsažených v synoviální kapalině při současné přítomnosti dalších proteinů. Jelikož metody aplikované v předchozích studiích neumožňovaly separovat jednotlivé složky maziva, byla vyvinuta optická měřící metoda na principu fluorescenční mikroskopie. Z důvodu verifikace metody byly provedeny dvě nezávislé studie zaměřené na měření tloušťky mazacího filmu a dělení maziva na výstupu mazaného kontaktu. Z důvodu určitých limitací fluorescenční mikroskopie byla dále využita i metoda optické interferometrie, jejíž využití je ilustrováno ve studii zabývající se formováním mazacího filmu v náhradách kyčelního klubu při uvažování reálné konformity třecích povrchů. Závěrečná část práce představuje nový metodologický přístup založený na in situ pozorování kontaktní oblasti umožňující popsat roli jednotlivých proteinů ve vztahu k vývoji tloušťky mazacího filmu. Práce obsahuje originální výsledky, které přináší nové poznání v oblasti biotribologie náhrad kyčelního kloubu vedoucí k dalšímu vývoji implantátů při snaze zabránit jejich selhání v důsledku omezené životnosti.
|
|
|
The Effect of Synovial Fluid Constituents on Lubrication of Hip Joint Replacements
Nečas, David ; Hartl, Martin (advisor)
Dizertační práce se zabývá mechanismy mazání v náhradách kyčelního kloubu. Byla provedena systematická studie formování proteinového filmu při zahrnutí různých materiálů a provozních podmínek. Hlavní pozornost je přitom věnována roli jednotlivých proteinů obsažených v synoviální kapalině při současné přítomnosti dalších proteinů. Jelikož metody aplikované v předchozích studiích neumožňovaly separovat jednotlivé složky maziva, byla vyvinuta optická měřící metoda na principu fluorescenční mikroskopie. Z důvodu verifikace metody byly provedeny dvě nezávislé studie zaměřené na měření tloušťky mazacího filmu a dělení maziva na výstupu mazaného kontaktu. Z důvodu určitých limitací fluorescenční mikroskopie byla dále využita i metoda optické interferometrie, jejíž využití je ilustrováno ve studii zabývající se formováním mazacího filmu v náhradách kyčelního klubu při uvažování reálné konformity třecích povrchů. Závěrečná část práce představuje nový metodologický přístup založený na in situ pozorování kontaktní oblasti umožňující popsat roli jednotlivých proteinů ve vztahu k vývoji tloušťky mazacího filmu. Práce obsahuje originální výsledky, které přináší nové poznání v oblasti biotribologie náhrad kyčelního kloubu vedoucí k dalšímu vývoji implantátů při snaze zabránit jejich selhání v důsledku omezené životnosti.
|
|
|
Lubrication of hip joint replacements
Rebenda, David ; Hartl, Martin (referee) ; Vrbka, Martin (advisor)
This thesis deals with the experimental study of lubrication of hip joint replacements. The influence of the synovial fluid composition and the head material to the lubricating film thickness were asssesed by using a pendulum hip joint simulator. Both of these effects were assesed under static and dynamic loading conditions. The experimental results showed that the movement of the head against the cup is unnecessary for the separation of the rubbing surfaces by a layer of adsorbed proteins. Composition of the synovial fluid then significantly influences the thickness of the lubricating film. Two opposite extremes have been observed during tests with two model synovial fluids. The first fluid formed a very strong lubricating film. The second sample almost prevent adsorption of proteins and consequently formed only very thin lubricating film. The influence of the material is noticeable when comparing the results obtained with a metal head and ceramic heads. Metal head formes under the same conditions thicker lubricating film. This evidence may be partly influenced by different diametrical clearances, which were in the case of ceramic heads higher.
|
|
|
Effect of femoral head size on friction and lubrication in THR
Bartošík, Jan ; Dzimko, Marián (referee) ; Vrbka, Martin (advisor)
This diploma thesis concerns itself with the experimental study of friction and lubrication in the artificial hip joint depending on the head size. Measurements were made in a hip joint simulator based on the principle of pendulum. For the friction measurements artificial joints, made from three material combinations and two diameters, from two companies were used. The measurements show that the material combination has a more significant effect to friction coefficient than the head size. Using a bigger head size shows a decrease in friction coefficient for all material combinations when compared to a smaller head size. For the measurement of lubrication film the colorimetric interferometry was applied. A metal-on-glass contact pair was used, where the glass cups were made according to the real measurements of the joint cups. Four types of hip replacements with diameters of 28 and 36 mm with two different diametral clearance were measured during a constant motion of 210 seconds. Measurements show, that the lubrication film in the hip joint with a small diametral clearance increases very fast over the 800 nm value. Contact surfaces in the hip joint with a large diametral clearance aren’t separated by the lubrication film, resulting in a damage of the chromium coating in cup. A thick lubrication film results in a higher friction coefficient, when compared with hip joints with a very thin or no lubrication film.
|
|
|
Experimental study of friction and lubrication in THR
Urban, Filip ; Čermák, Jan (referee) ; Vrbka, Martin (advisor)
This work analyzes problems of friction and lubrication of total hip replacement (THR). At first, experimental study of friction coefficient under various conditions was conducted using hip joint simulator based on principle of pendulum. After that, lubrication film development was observed, using colorimetric interferometry with head from THR and glass cup with respect of geometry and clearance to cups made originally for THR. With respect to research study [25] it was found that increasing contact conformity leads to increased film thickness. Also protein adsorption on articulating surfaces was observed. Thanks to adsorption 80 nm film thickness was measured even if relative surface speed was zero. Furthermore protein aggregation was observed on the border of contact zone, similar aggregations were observed by Myant et al. [29] or Vrbka et al. [25]. These aggregations are formed when lubricant is under shear stress and it can positively affect film thickness. If the relative motion of articulating surfaces is not sufficient, the protein layer can`t be refreshed enough and film thickness start decreasing. Coefficient of friction 0,13 was measured when lubricating film development was observed. Close to this value are material combinations metal on polyethylene and metal on metal.
|
|
|
Study of Friction in Hip Joint Replacements
Balounová, Hana ; Dzimko, Marián (referee) ; Vrbka, Martin (advisor)
Diploma thesis deals with analysis of coefficient of friction in total hip prosthesis for several materials bearing with presence of bovine serum as substitute of synovial fluid occurred in natural joint. Behavior of coefficient of friction is observed on Mini Traction Machine. Results are plotted at graphs representing dependence of coefficient of friction on time. There are described effects of several kinematic conditions, the influence of used material and the effect of the method of contact lubrication. The experiments analyze how the formation of lubricant film with a layer of adsorbed protein affects coefficient of friction.
|
|
|
Mapping of lubricating film thickness of human big joints replacements
Bosák, Dalibor ; Hartl, Martin (referee) ; Vrbka, Martin (advisor)
This master’s thesis describes mechanism of lubricating film forming and its thickness in contact of a metal hip joint ball and a glass disc with chromium layer with presence of bovine serum as substitute of synovial fluid occured in a natural joint. Lubricating film thickness is evaluated by a thin film colorimetric interferometry, results are ploted at graphs representing dependence of lubricating film thickness on experiment duration or on mutual speed of articulating surfaces. There is described the influence of concentration of bovine serum and different kinematic conditions on lubricating film forming. From observed interferograms is apparent the adsorption of proteins to glass disc and femoral head surfaces, denaturation and formation of protein aggregations affecting the residual lubricating film thickness.
|
|
|
Analysis of biotribological properties of artificial hip joint
Laštůvka, Jan ; Burša, Jiří (referee) ; Návrat, Tomáš (advisor)
The development of total hip arthroplasty has reached a state when quality prostheses are made, whose longevity is influenced significantly by material properties, design, component fixation and rate of wear of the articulating surfaces. It is the wear rate which is the most important factor influencing successful results for the use of total hip prostheses. The aim of this thesis is to perform a research on the various combinations of hip prostheses and its loading conditions. Also an experimental measurements of Bovine serum lubricating film thickness between the artificial femoral head and a glass disc are performed for different contact kinematic conditions.
|
|
|
History of hip joint replacements
Kohout, Jiří ; Urban, Filip (referee) ; Vrbka, Martin (advisor)
In this bachelor´s thesis is solved problem of friction, lubrication, wear and history of hip replacement. History is described from the second half of 18th century and there was an effort to include every important milestones that affected development of the alloplastic of hip joint. Beside this development is also observed volume wear of hip joint. History of lubrication and friction is watched from first experiment, which measured these factors it means mid-20th century.
|