Mechanical properties of doped piezoceramics based on BaTiO3
Zeman, Dominik ; Chlup, Zdeněk (referee) ; Drdlík, Daniel (advisor)
This master‘s thesis deals with study of basic physical, microstructural and mechanical properties of doped piezoceramic materials based on BaTiO3 prepared by electrophoretic deposition. The dopants used were rare earth oxides, i.e. Eu2O3, Er2O3, CeO2, Dy2O3 and Tb4O7 in amounts 1, 3 and 5 wt. %. The influence of dopants and their amount on density, phase composition, mean grain size, hardness, elastic modulus, fracture toughness, and flexural strength was examined. Suitable dopant choice enabled decrease in mean grain size and increase in relative density, hardness, elastic modulus, fracture toughness and flexural strength of sintered specimens. Relative densities up to 99 %, mean grain size below 1 m, hardness up to 13,1 GPa, elastic modulus up to 199 GPa, fracture toughness above 1 MPa·m1/2 and flexural strength above 115 MPa were achieved.
|
|
Fabrication and properties of doped piezoceramics based on BaTiO3
Mařák, Vojtěch ; Chlup, Zdeněk (referee) ; Drdlík, Daniel (advisor)
This diploma thesis deals with the preparation of doped piezoceramic materials based on BaTiO3 using electrophoretic deposition. Five rare earth oxides, i.e. Er2O3, Dy2O3, Eu2O3, Tb407 and CeO2, were used as dopants in amounts of 1, 3, and 5 wt. %. The prepared deposits were evaluated in terms of preparation methodology, high temperature dilatometry, X-ray diffraction analysis, relative density, mean grain size, hardness and fractographic analysis. The study of dilatometric curves described the sintering behavior and its changes at different material compositions. X-ray diffraction analysis revealed a tetragonal phase in all samples; the tetragonality of the BaTiO3 crystalline cell decreased with dopant content. By a suitable choice of dopant, it was possible to significantly increase the relative density of sintered samples, their hardness and at the same time prevent the samples from coarsening of the microstructure during heat treatment. A relative density up to 98 %, a mean grain size below 1 m and a hardness of over 10 GPa were achieved. Analysis of the fracture surfaces revealed that the fracture mode was transcrystalline for the most of studied materials; only the samples doped with cerium dioxide had fracture surfaces with both transcrystalline and intercrystalline fracture modes. Based on the obtained results, a suitable composition of the material for the intended use in a layered piezoceramic harvester was identified, which, in addition to the BaTiO3 layers, consists of functionally-protective Al2O3 and ZrO2 layers.
|