Difúze 99Mo ve teplně zpracované slitině Fe76Mo8Cu1B15
Čermák, Jiří ; Stloukal, Ivo
Ion beam sputtering by Ar+ ions was used to investigate 99Mo tracer diffusion in Fe76Mo8Cu1B15 alloy in the temperature range 548 – 648 K. The experimental samples were prepared from ribbons of Fe76Mo8Cu1B15 alloy in as quenched state q, and after pre-annealing at 683 K for 1 h (state a1) and at 743 K for 1 h (state a2). The penetration profiles were obtained using serial sectioning method and consist of two parts suggesting that two different diffusion paths are operating. The Mo short-circuit diffusivity P was evaluated using both LeClaire’s analysis and Divinski’s theory derived for transition type-A/B regime in coarse-grained materials.
|
|
| |
|
|
Difúzní studie Fe a Mo ve slitině Fe76Mo8B15Cu1
Čermák, Jiří ; Stloukal, Ivo
59Fe and 99Mo tracer diffusion in Fe76Mo8B15Cu1 alloy was studied using serial sectioning method in the temperature range 527 – 649 K. The ribbon-like samples were annealed at 695 K for 1 and 5 hours before the diffusion experiments; the volume fraction of crystalline phase was checked by the Mössbauer spectroscopy. Concentration profiles obtained by sputtering by Ar+ ions in a glow discharge show two distinct branches suggesting that two diffusion paths are operating.
|
|
| |
guest ::