Relationship between Structure and Properties of cast Ni-alloys
Smékalová, Jana ; Hutařová, Simona (referee) ; Podrábský, Tomáš (advisor)
Nickel superalloys are developed for conditions which request the corrosion resistance, the heat-resisting and the creep-resisting material. They are used for components of air turbine motors and internal combustion turbines. The efficiency of these mechanisms is elevated with increasing combustion temperature so their development is accentuated. This thesis is concerned with a relationship between a structure and properties of nickel superalloys Inconel 713LC and Inconel 738LC in this thesis.
|
|
|
Fatigue failure mechanism of nickel-based superalloy Inconel 713LC under 800°C
Smékalová, Jana ; Juliš, Martin (referee) ; Hutařová, Simona (advisor)
Nickel superalloys are used for high-temperature application in energetic and aerospace industry. They are exposed to aggressive environment at high temperatures with the interactions between fatigue and creep processes, high-temperature oxidation, corrosion and erosion. Lifetime extension of such strained parts while increasing the performance of particular machine is possible by applying protective surface coatings. The subject of this work is to investigate the fatigue failure mechanisms of superalloy Inconel 713LC at 800 °C and to compare these mechanisms between material with a protective coating based on Al-Si and material without coating. The location of initiation fatigue cracks, their propagation and the fatigue crack propagation rate in some areas were analyzed by optical microscopy, scanning electron microscopy and confocal laser scanning microscopy. Based on previous research it was found that the application of the coating AlSi has a positive effect on lifetime of alloy Inconel 713LC. These results were confirmed and estimated in the diploma thesis.
|
|
|
Fatigue failure mechanism of nickel-based superalloy Inconel 713LC under 800°C
Smékalová, Jana ; Juliš, Martin (referee) ; Hutařová, Simona (advisor)
Nickel superalloys are used for high-temperature application in energetic and aerospace industry. They are exposed to aggressive environment at high temperatures with the interactions between fatigue and creep processes, high-temperature oxidation, corrosion and erosion. Lifetime extension of such strained parts while increasing the performance of particular machine is possible by applying protective surface coatings. The subject of this work is to investigate the fatigue failure mechanisms of superalloy Inconel 713LC at 800 °C and to compare these mechanisms between material with a protective coating based on Al-Si and material without coating. The location of initiation fatigue cracks, their propagation and the fatigue crack propagation rate in some areas were analyzed by optical microscopy, scanning electron microscopy and confocal laser scanning microscopy. Based on previous research it was found that the application of the coating AlSi has a positive effect on lifetime of alloy Inconel 713LC. These results were confirmed and estimated in the diploma thesis.
|
|
|
Relationship between Structure and Properties of cast Ni-alloys
Smékalová, Jana ; Hutařová, Simona (referee) ; Podrábský, Tomáš (advisor)
Nickel superalloys are developed for conditions which request the corrosion resistance, the heat-resisting and the creep-resisting material. They are used for components of air turbine motors and internal combustion turbines. The efficiency of these mechanisms is elevated with increasing combustion temperature so their development is accentuated. This thesis is concerned with a relationship between a structure and properties of nickel superalloys Inconel 713LC and Inconel 738LC in this thesis.
|
|
|
Contrastive Analysis of Expressing Impersonality in Czech and Spanish
SMÉKALOVÁ, Jana
This diploma thesis is focused on the ways of expressing impersonality in Czech and Spanish language. The main aim of this thesis is to capture and compare the amount and possibilities of expressing the impersonality in both languages. The author also focuses on the description of the deagentive constructions followed by analysis of these constructions in authentic texts. The results of the research were achieved with the help of specialised literature, original Czech and Spanish texts which form the base for the comparative analysis.
|