Experimental manufacturing of multiphase Ni-Si based layers
 Rončák, Ján ; Moravčík, Igor (referee) ; Jan, Vít (advisor)
The diploma thesis deals with the preparation of the composite material based on the NiSi system using powder metallurgy supplemented by the sintering with the usage of SPS method (spark plasma sintering). Theoretical part contains general information about the mechanical-chemical process and sintering, while materials and methods used for experimental observation are explained in a separate chapter. Experimental part explains the procedure of the experiment and selected parameters of individual processes. In the experiment, two powder mixtures were created in order to form the NiSi phase in the maximum possible amount of powder material. After successfully reaching presence of the NiSi phase in the range of 87 to 89 wt. %, both mixtures were used to produce sintered samples at temperatures from 700 to 900 °C. Experiments showed the best results for sample number 2, which was sintered at 900 °C for 4 minutes. Resulting porosity was 0.9 % and hardness reached a maximum value of 718 HV 1. However, all sintered samples show cracks at room temperature associated with increased brittleness of the material.
Detailed record
Experimental manufacturing of multiphase Ni-Si based layers
 Rončák, Ján ; Moravčík, Igor (referee) ; Jan, Vít (advisor)
The diploma thesis deals with the preparation of the composite material based on the NiSi system using powder metallurgy supplemented by the sintering with the usage of SPS method (spark plasma sintering). Theoretical part contains general information about the mechanical-chemical process and sintering, while materials and methods used for experimental observation are explained in a separate chapter. Experimental part explains the procedure of the experiment and selected parameters of individual processes. In the experiment, two powder mixtures were created in order to form the NiSi phase in the maximum possible amount of powder material. After successfully reaching presence of the NiSi phase in the range of 87 to 89 wt. %, both mixtures were used to produce sintered samples at temperatures from 700 to 900 °C. Experiments showed the best results for sample number 2, which was sintered at 900 °C for 4 minutes. Resulting porosity was 0.9 % and hardness reached a maximum value of 718 HV 1. However, all sintered samples show cracks at room temperature associated with increased brittleness of the material.
Detailed record

Interested in being notified about new results for this query?
Subscribe to the RSS feed.
Digital Repository :: Search :: Submit :: Personalize :: Help
Powered by Invenio v1.1.2
Maintained by admin.invenio@techlib.cz
This site is also available in the following languages:
Česky  English