Vida, Mikuláš ; Kučera, František (referee) ; Jančář, Josef (advisor)
The aim of this bachelor thesis was the investigation of changes of mechanical and rheological properties of nanocomposites based on PMMA, where filler was fumed silica of four types (different surface area and producer). The thesis focuses on the theoretical part of the current state of research, preparation and properties of nanocomposites. The solvent method was chosen for the preparation of nanocomposites, where silica was mixed with dissolved PMMA. Tensile mechanical properties were measured below Tg, while viscoelastic response was measured above Tg. Silica had not significant influence on the modulus below Tg, but above Tg (180 °C) both modulus, storage and loss, have increased with increasing silica content and with increasing frequency (0,1–100 Hz). The particle size and surface area of silica in a content of 1 % influenced storage modulus of nanocomposites more with respect to the content of 2 %. For samples containing 1 % showed that the significant role played particle size and surface area of silica. The greatest increase of storage and loss modulus of PMMA was reached for silica M-5 in content 1 %. All type of silica decreased tensile strength and strain with increasing silica content in the same way.
|
|
|
Automotive plastics with increased scratch resistance
Vida, Mikuláš ; Kučera, František (referee) ; Jančář, Josef (advisor)
The aim of this bachelor thesis was the investigation of changes of mechanical and rheological properties of nanocomposites based on PMMA, where filler was fumed silica of four types (different surface area and producer). The thesis focuses on the theoretical part of the current state of research, preparation and properties of nanocomposites. The solvent method was chosen for the preparation of nanocomposites, where silica was mixed with dissolved PMMA. Tensile mechanical properties were measured below Tg, while viscoelastic response was measured above Tg. Silica had not significant influence on the modulus below Tg, but above Tg (180 °C) both modulus, storage and loss, have increased with increasing silica content and with increasing frequency (0,1–100 Hz). The particle size and surface area of silica in a content of 1 % influenced storage modulus of nanocomposites more with respect to the content of 2 %. For samples containing 1 % showed that the significant role played particle size and surface area of silica. The greatest increase of storage and loss modulus of PMMA was reached for silica M-5 in content 1 %. All type of silica decreased tensile strength and strain with increasing silica content in the same way.
|
guest ::