Hot dip galvanizing of the steel construction
Pometlo, Stanislav ; Vyplašil, Evžen (referee) ; Kubíček, Jaroslav (advisor)
This master´s thesis deals with hot dip galvanizing of steel constructions and their protection from corrosion. This work describes the origin of corrosion of steel and its corrosion in different areas and presents degreasing and pickling before hot dip galvanization. It describes possibilities of making zinc layer by the wet and draw method of hot dip galvanization. Furthermore, it puts forward reactions between zinc and iron, possible defects of the zinc layer and influence of the hot dip galvanizing on the steel constructions. The experimental part examines the influence of the hydrogen charging on the material and the time of the flux operation on the quality of layer. The work further analyses the changing of mechanical properties of steels Hardox 500 and Weldox 700 as a result of the hydrogen embrittlement during pickling by the hydrochloric acid.
|
|
|
The technology of hot-dip galvanizing
Pometlo, Stanislav ; Osička, Karel (referee) ; Mouralová, Kateřina (advisor)
This thesis deals with the technology of hot-dip galvanizing. At the beginning of this work views into the history of hot-dip galvanizing and analysis of known technologies about applying of melted zinc into the surface of material. It further describes modification for surface before application of zinc´s coating. In the next part of the work are summarized the most common corrosions of hot-dip galvanized material. The work follows up the difficultness of operation for hot-dip galvanizing device. At the end of work describes cooperation with Alka Holding s. r. o.
|
|
|
Hot dip galvanizing of the steel construction
Pometlo, Stanislav ; Vyplašil, Evžen (referee) ; Kubíček, Jaroslav (advisor)
This master´s thesis deals with hot dip galvanizing of steel constructions and their protection from corrosion. This work describes the origin of corrosion of steel and its corrosion in different areas and presents degreasing and pickling before hot dip galvanization. It describes possibilities of making zinc layer by the wet and draw method of hot dip galvanization. Furthermore, it puts forward reactions between zinc and iron, possible defects of the zinc layer and influence of the hot dip galvanizing on the steel constructions. The experimental part examines the influence of the hydrogen charging on the material and the time of the flux operation on the quality of layer. The work further analyses the changing of mechanical properties of steels Hardox 500 and Weldox 700 as a result of the hydrogen embrittlement during pickling by the hydrochloric acid.
|
|
|
The technology of hot-dip galvanizing
Pometlo, Stanislav ; Osička, Karel (referee) ; Mouralová, Kateřina (advisor)
This thesis deals with the technology of hot-dip galvanizing. At the beginning of this work views into the history of hot-dip galvanizing and analysis of known technologies about applying of melted zinc into the surface of material. It further describes modification for surface before application of zinc´s coating. In the next part of the work are summarized the most common corrosions of hot-dip galvanized material. The work follows up the difficultness of operation for hot-dip galvanizing device. At the end of work describes cooperation with Alka Holding s. r. o.
|