| Home > Academic theses (ETDs) > Bachelor's theses > Vliv rozpouštěcího žíhaní na rozložení fází u duplexních austeniticko-feritických ocelí |
Original title:
Vliv rozpouštěcího žíhaní na rozložení fází u duplexních austeniticko-feritických ocelí
Translated title: The influence of solution annealing on phase distribution in duplex austenitic-ferritic steels
Authors: Kareš, Michal ; Kaněra, Miloš (referee) ; Myška, Martin (advisor)
Document type: Bachelor's theses
Year: 2026
Language: cze
Publisher: Vysoké učení technické v Brně. Fakulta strojního inženýrství
Abstract: [cze] [eng]
Keywords: and Brinell hardness testing. Within the framework of optical metallography; and the effect of individual heat treatment regimes on the resulting hardness of the material. The experimental part included a comparison of the as-cast condition and samples subjected to different solution annealing regimes. The evaluation was carried out using optical light microscopy; The aim of this bachelor’s thesis was to assess the effect of solution annealing on the microstructure and properties of cast hyperduplex stainless steel Grade 7A according to the American ASTM A890 standard. The main focus is the relationship between the standard-based approach to heat treatment and equilibrium thermodynamic simulation. Particular attention was paid to changes in phase composition; the occurrence of undesirable intermetallic phases; two approaches were used to determine the approximate area fraction of phases: software-based analysis performed by an operator and AI-assisted visual evaluation of metallographic images.; with emphasis on controlling the presence of the sigma phase; X-ray diffraction analysis; a to metoda analýzy operátorem s využitím softwaru a asistované vizuální hodnocení metalografických snímků pomocí umělé inteligence.; Cílem této bakalářské práce bylo posouzení vlivu rozpouštěcího žíhání na mikrostrukturu a vlastnosti lité hyperduplexní korozivzdorné oceli jakostní třídy 7A podle americké normy ASTM A890. Hlavní myšlenkou je souvislost mezi normovým přístupem k tepelnému zpracování a rovnovážnou termodynamickou simulací. Pozornost byla zaměřena zejména na změnu fázového složení; rentgenové difrakční analýzy a zkoušky tvrdosti dle Brinella. V rámci optické metalografie byly pro stanovení orientačního plošného zastoupení fází použity dva přístupy; výskyt nežádoucích intermetalických fází s důrazem na kontrolu přítomnosti intermetalické fáze sigma a vliv jednotlivých režimů tepelného zpracování na výslednou tvrdost materiálu. Výzkumná část zahrnovala porovnání litého stavu a vzorků po různých režimech rozpouštěcího žíhání. Hodnocení bylo provedeno pomocí optické světelné mikroskopie
Institution: Brno University of Technology (web)
Document availability information: Fulltext is available in the Brno University of Technology Digital Library.
Original record: http://hdl.handle.net/11012/257491
Permalink: http://www.nusl.cz/ntk/nusl-774170
The record appears in these collections:
Universities and colleges > Public universities > Brno University of Technology
Academic theses (ETDs) > Bachelor's theses
Translated title: The influence of solution annealing on phase distribution in duplex austenitic-ferritic steels
Authors: Kareš, Michal ; Kaněra, Miloš (referee) ; Myška, Martin (advisor)
Document type: Bachelor's theses
Year: 2026
Language: cze
Publisher: Vysoké učení technické v Brně. Fakulta strojního inženýrství
Abstract: [cze] [eng]
Keywords: and Brinell hardness testing. Within the framework of optical metallography; and the effect of individual heat treatment regimes on the resulting hardness of the material. The experimental part included a comparison of the as-cast condition and samples subjected to different solution annealing regimes. The evaluation was carried out using optical light microscopy; The aim of this bachelor’s thesis was to assess the effect of solution annealing on the microstructure and properties of cast hyperduplex stainless steel Grade 7A according to the American ASTM A890 standard. The main focus is the relationship between the standard-based approach to heat treatment and equilibrium thermodynamic simulation. Particular attention was paid to changes in phase composition; the occurrence of undesirable intermetallic phases; two approaches were used to determine the approximate area fraction of phases: software-based analysis performed by an operator and AI-assisted visual evaluation of metallographic images.; with emphasis on controlling the presence of the sigma phase; X-ray diffraction analysis; a to metoda analýzy operátorem s využitím softwaru a asistované vizuální hodnocení metalografických snímků pomocí umělé inteligence.; Cílem této bakalářské práce bylo posouzení vlivu rozpouštěcího žíhání na mikrostrukturu a vlastnosti lité hyperduplexní korozivzdorné oceli jakostní třídy 7A podle americké normy ASTM A890. Hlavní myšlenkou je souvislost mezi normovým přístupem k tepelnému zpracování a rovnovážnou termodynamickou simulací. Pozornost byla zaměřena zejména na změnu fázového složení; rentgenové difrakční analýzy a zkoušky tvrdosti dle Brinella. V rámci optické metalografie byly pro stanovení orientačního plošného zastoupení fází použity dva přístupy; výskyt nežádoucích intermetalických fází s důrazem na kontrolu přítomnosti intermetalické fáze sigma a vliv jednotlivých režimů tepelného zpracování na výslednou tvrdost materiálu. Výzkumná část zahrnovala porovnání litého stavu a vzorků po různých režimech rozpouštěcího žíhání. Hodnocení bylo provedeno pomocí optické světelné mikroskopie
Institution: Brno University of Technology (web)
Document availability information: Fulltext is available in the Brno University of Technology Digital Library.
Original record: http://hdl.handle.net/11012/257491
Permalink: http://www.nusl.cz/ntk/nusl-774170
The record appears in these collections:
Universities and colleges > Public universities > Brno University of Technology
Academic theses (ETDs) > Bachelor's theses
Record created 2026-06-14, last modified 2026-07-24