Milling optimization of ceramic blanks
Ráčková, Jana ; Pouchlý, Václav (referee) ; Trunec, Martin (advisor)
The master thesis deals mainly with the optimization of machining of ceramic semi-finished products from ZrO2 and Al2O3. The first part with literary research, which describes the steps of the technology of forming ceramic bodies, especially the gelcasting method. The thesis describes possibilities of milling of ceramic materials using CNC technology. The thesis describes the dependence of acquired roughness on bodies and used machining strategies. The best roughness parameters on ZrO2 samples were obtained after they were calcined at 900 ° C, while the lowest roughness was obtained on the samples in the unprotected state for the Al2O3 samples. Samples machined with a spherical milling cutter showed surface roughness Ra = 1 m for ZrO2 and Ra = 1.3 m for Al2O3. It also describes the possibility of machining sharp-edged shapes and fine details where the best results are achieved on ZrO2 samples engraved at 900 and 1100 °C. Tool wear was particularly important when machining samples of Al2O3 ignited at temperatures above 800 °C.
|
|
|
Milling optimization of ceramic blanks
Ráčková, Jana ; Pouchlý, Václav (referee) ; Trunec, Martin (advisor)
The master thesis deals mainly with the optimization of machining of ceramic semi-finished products from ZrO2 and Al2O3. The first part with literary research, which describes the steps of the technology of forming ceramic bodies, especially the gelcasting method. The thesis describes possibilities of milling of ceramic materials using CNC technology. The thesis describes the dependence of acquired roughness on bodies and used machining strategies. The best roughness parameters on ZrO2 samples were obtained after they were calcined at 900 ° C, while the lowest roughness was obtained on the samples in the unprotected state for the Al2O3 samples. Samples machined with a spherical milling cutter showed surface roughness Ra = 1 m for ZrO2 and Ra = 1.3 m for Al2O3. It also describes the possibility of machining sharp-edged shapes and fine details where the best results are achieved on ZrO2 samples engraved at 900 and 1100 °C. Tool wear was particularly important when machining samples of Al2O3 ignited at temperatures above 800 °C.
|
|
| |
|
| |
|
| |
guest ::
RSS feed.