Printed transparent oxide conductors
Bartoš, Radim ; Pekárková, Jana (referee) ; Dzik, Petr (advisor)
Thin films of tin oxide doped by fluorine or antimony were prepared by spincoating technique and material printing technique. Plenty of inorganic and organic coumpouds were used as precursors of fluorine and antimony. Sheet resistence of films were measured by 4-probe method and film thickness were determined by contact profilometer. Films were analyzed by Xray diffraction (XRD) and scan electron microscopy (SEM).
|
|
|
Fabrication and characterization of oxidic conductive layers
Bartoš, Radim ; Gemeiner,, Pavol (referee) ; Dzik, Petr (advisor)
Liquid composition for antimony doped tin oxide solgel deposition was prepared. Anorganic precursors of tin and antimony were used (tin(IV) chloride, antimony(III) chloride). ATO nanoparticles were dispergated in composition. This composition was used for spincoating deposition of thin films. Composition was analyzed by thermal analysis TGA and DSC. Sheet resistence of prepared samples were examined by four probe sensing. RMS roughness and thickness was measured by profilometry. Samples were analyzed by scan electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Transmittance and haze were measured and calculated by UV-VIS spektrometry with integration sphere.
|
|
|
Fabrication and characterization of oxidic conductive layers
Bartoš, Radim ; Gemeiner,, Pavol (referee) ; Dzik, Petr (advisor)
Liquid composition for antimony doped tin oxide solgel deposition was prepared. Anorganic precursors of tin and antimony were used (tin(IV) chloride, antimony(III) chloride). ATO nanoparticles were dispergated in composition. This composition was used for spincoating deposition of thin films. Composition was analyzed by thermal analysis TGA and DSC. Sheet resistence of prepared samples were examined by four probe sensing. RMS roughness and thickness was measured by profilometry. Samples were analyzed by scan electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Transmittance and haze were measured and calculated by UV-VIS spektrometry with integration sphere.
|
|
|
Printed transparent oxide conductors
Bartoš, Radim ; Pekárková, Jana (referee) ; Dzik, Petr (advisor)
Thin films of tin oxide doped by fluorine or antimony were prepared by spincoating technique and material printing technique. Plenty of inorganic and organic coumpouds were used as precursors of fluorine and antimony. Sheet resistence of films were measured by 4-probe method and film thickness were determined by contact profilometer. Films were analyzed by Xray diffraction (XRD) and scan electron microscopy (SEM).
|