Mechanical response of glass fiber-reinforced polymer composite
Širjovová, Veronika ; Svěrák, Tomáš (referee) ; Čech, Vladimír (advisor)
The bachelor thesis is concerned with mechanical properties of glass fiber-reinforced polymer composites depending on the surface modification of fibers and the volume fraction of fibers in the composite. The tested samples in a form of composite beams were consisted of polyester matrix reinforced with long glass fibers without surface treatment (unsized) and with commercial sizing. Shear and flexural tests were employed to evaluate adhesion at the fiber-matrix interface. The theoretical part focuses on literary search for composites, their components (matrix, reinforcement, interphase) and methods of testing their mechanical properties. The experimental part describes used materials, procedures and methods. In the result part, an assessment of the influence of the given conditions on the shear and flexural strength of the composite is summarized.
|
|
|
Plasma surface modification of glass fibers and its optimization
Širjovová, Veronika ; Knob, Antonín (referee) ; Čech, Vladimír (advisor)
Diploma thesis deals with glass fiber surface modification using plasma-enhanced chemical vapor deposition in order to prepare functional interface that enhances the properties of polymer composites. The effect of deposition conditions on shear strength was observed with respect to the chemical composition of the deposited film. Thin films were deposited on planar substrates and fibers using monomer tetravinylsilane in a mixture with oxygen at selected power of plasma discharge. Chemical composition of prepared material was analyzed by infrared spectroscopy. Planar substrate film adhesion was measured using the scratch test. The composite sample was prepared by embedding the surface modified fibers in unsaturated polyester resin, followed by the curing process. The cured composite sample underwent the short beam shear test.
|
|
|
Plasma surface modification of glass fibers and its optimization
Širjovová, Veronika ; Knob, Antonín (referee) ; Čech, Vladimír (advisor)
Diploma thesis deals with glass fiber surface modification using plasma-enhanced chemical vapor deposition in order to prepare functional interface that enhances the properties of polymer composites. The effect of deposition conditions on shear strength was observed with respect to the chemical composition of the deposited film. Thin films were deposited on planar substrates and fibers using monomer tetravinylsilane in a mixture with oxygen at selected power of plasma discharge. Chemical composition of prepared material was analyzed by infrared spectroscopy. Planar substrate film adhesion was measured using the scratch test. The composite sample was prepared by embedding the surface modified fibers in unsaturated polyester resin, followed by the curing process. The cured composite sample underwent the short beam shear test.
|
|
|
Mechanical response of glass fiber-reinforced polymer composite
Širjovová, Veronika ; Svěrák, Tomáš (referee) ; Čech, Vladimír (advisor)
The bachelor thesis is concerned with mechanical properties of glass fiber-reinforced polymer composites depending on the surface modification of fibers and the volume fraction of fibers in the composite. The tested samples in a form of composite beams were consisted of polyester matrix reinforced with long glass fibers without surface treatment (unsized) and with commercial sizing. Shear and flexural tests were employed to evaluate adhesion at the fiber-matrix interface. The theoretical part focuses on literary search for composites, their components (matrix, reinforcement, interphase) and methods of testing their mechanical properties. The experimental part describes used materials, procedures and methods. In the result part, an assessment of the influence of the given conditions on the shear and flexural strength of the composite is summarized.
|