Study of optical properties of thin films of perovskiteFAPbBr3 precursors
Smolková, Denisa ; Čech, Vladimír (referee) ; Zmeškal, Oldřich (advisor)
This thesis examines the preparation of thin layers of material for photovoltaic applications with focused on perovskites and determining their optical properties. Basic information about the photovoltaic panels, especially about the perovskites, and the preparation of thin layers is supplied in the theoretical section. This section includes description of optical properties and the main method of study of optical properties, spectroscopic ellipsometry. Experimental section is focused on the preparation of thin layers of perovskites FAPbBr3 and its precursors by spin-coating. Optical properties are evaluated using profilometry, UV VIS spectrometry and spectroscopic ellipsometry. The conclusion summarizes the results of this experiment with focused on comparison of ellipsometric spectrums of perovskites and its precursors.
|
|
|
Study of plasma species by mass spectroscopy
Bureš, Michal ; Čáslavský, Josef (referee) ; Čech, Vladimír (advisor)
Plasma polymer films of tetravinylsilane and mixture of tetravinylsilane and oxygen gas were deposited on silicon wafers. Oxygen gas was mixed in tetravinylsilane to improve the compatibility of thin films on glass substrates. Mass spectroscopy was employed during the cleaning of the deposition chamber to check residual gases and process gases, during plasma deposition to monitor neutral plasma species and to follow plasma stability.
|
|
|
Fabrication of Nanostructures and Nanodevices for Nanoelectronics and Spintronics
Lišková, Zuzana ; Červenka, Jiří (referee) ; Čech, Vladimír (referee) ; Šikola, Tomáš (advisor)
The thesis deals with preparation of graphene nanostructures and their applications in the measurement of transport properties of graphene. The contacts for measurement of resistance are fabricated by electron beam lithography on graphene exfoliated flakes, CVD graphene layers and grains. Graphene is also shaped using the same method. Resistivity of the layer, concentration and mobility of charge carriers are determined by different approaches. Hysteresis appearing in dependence of resistivity on the gate voltage is discussed as well. A significant part of the work is dedicated to monitoring the response of graphene resistance to relative humidity changes and potential use of graphene as a sensor of relative humidity.
|
|
|
Plasma-enhanced chemical vapor deposition using TVS/Ar and TVS/O2 mixtures
Sadílek, Jakub ; Salyk, Ota (referee) ; Čech, Vladimír (advisor)
Tato studie je zaměřena na základní výzkum přípravy a-SiC:H a a-SiCO:H slitin plazmových polymerů pomocí metody plazmochemické depozice z plynné fáze (PE-CVD). Tyto slitiny byly připravovány depozicí z monomeru tetravinylsilanu (TVS) a jeho směsí s kyslíkem a argonem při různých efektivních výkonech pulzního plazmatu. Připravené tenké vrstvy byly za účelem získání závislostí optických, mechanických a chemických vlastností na depozičních podmínkách zkoumány pomocí metod spektros-kopické elipsometrie (ELL), nanoindentace (NI), fotoelektronové spektrometrie (XPS) a Fourierovy transformované infračervené spektrometrie
|
|
|
Analysis of a-SiOC:H films by selected spectroscopic techniques
Ondreáš, František ; Zmeškal, Oldřich (referee) ; Čech, Vladimír (advisor)
This bachelor thesis deals with preparation of thin plasma polymer films on the basis of tetravinylsilane by plasma-enhanced chemical vapour deposition and film characterization by selected spectroscopic techniques. The theoretical part is a background research about plasma chemistry and spectroscopic methods of characterisation of thin plasma polymer films. The practical part consisted of preparation of two series of samples and their characterization. Prepared thin plasma polymer films were characterized by selected spectroscopic techniques. Thickness and optical constants were determined by spectroscopic elipsometry. Chemical structure was characterized by infrared spectroscopy. The results indicate the possibility of managing physico-chemical properties of thin plasma polymer films on the basis of tetravinylsilane by deposition conditions and thus possibility of preparation materials tailored to a variety of applications.
|
|
|
Infrared spectroscopy of thin films
Kiss, Andrej ; Čáslavský, Josef (referee) ; Čech, Vladimír (advisor)
Cílem této bakalářské práce je literární rešerše v oblasti tenkých vrstev, plazmochemické depozice z plynné fáze a infračervené spektroskopie Fourierovou transformací, a měření infračervených spekter tenkých vrstev a charakterizace jejich chemické struktury na základě změřených spekter. Pomocí infračervené spektroskopie Fourierovou transformací bylo měřeno pět vzorků tenkých polymerních vrstev z tetravinylsilanu, vytvořených na křemíkovém substrátu pomocí plazmochemické depozice z plynné fázi s efektivním výkonem v rozmezí od 2 W do 150 W. Měření odhalilo chemické vazby přítomné ve vzorcích a jak se struktura měnila s měnící se efektivním výkonem. Snížení absorpčních pásů s přítomností vodíku naznačuje zvýšení zesítění se zvýšeným efektivním výkonem. Také snížení absorpčních pásů s přítomností křemíku poskytuje důkaz pro zvýšení poměru C/Si. Tyto výsledky nám pomáhají porozumět charakteristikám těchto tenkých vrstev a přispívají k pochopení procesu plazmochemické depozice z plynné fáze.
|
|
|
Influence of glass fiber degradation on the mechanical response of a polymer composite
Součková, Lenka ; Knob, Antonín (referee) ; Čech, Vladimír (advisor)
The bachelor thesis studies the effect of fiber degradation with commercial sizing on the flexural properties of polymer composite based on unsaturated polyester resin reinforced with long unidirectionally oriented glass fibers. Fibres of age 23, 61, 67, 112 and 135 months were used to prepare a series of composite samples. The mechanical properties of a composite containing 40.5% % vol of fiber were determined using a three-point bending test defined by ASTM D790-17 standard. From the obtained data, the flexural strength, the flexural modulus and the flexural strain were evaluated. It has been found that the degradation of the fibers and their sizing leads to a reduction in flexural strength. This was due to the reduction of adhesion between the fibers and the matrix, thus also the quality of the interface, which caused insufficient stress transfer from the matrix to the fibre. The resulting difference in strength of composites with fibers aged 23 and 135 months was 0,19 GPa with respect to the origin value of 1,17 GPa. The obtained values were used to assess the correlation between the flexural strength of the composite and the shear strength. Pearson's correlation coefficient set at 0,71 corresponds to a strong correlation. The effect of fiber degradation on the flexural modulus has not been demonstrated.
|
|
|
Comparison of specialized actigraphs with wearable devices in quantitative sleep analysis
Čech, Vladimír ; Zvončák, Vojtěch (referee) ; Mikulec, Marek (advisor)
Actigraphy and smart wearable devices provide similar functionality in quantitative sleep analysis. This work aims to verify how common wearable devices stand in comparison with a specialized actigraph used in clinical practice. The actigraph used in this work was Geneactiv Original and it was used to compare the sleep analysis results of eleven commercially available devices. The measurements for nine of the measured devices lasted for one week. Two devices were measured for six days. During sleep, the device was worn on the same hand as the actigraph, and at the same time a sleep diary was kept, in which data on the time of lying down, the time of awakening and the number of awakenings per night were recorded. After a week of measurement, the data obtained from the actigraph were evaluated by software and then compared with the data provided by the second device. In this work, data of total sleep time, sleep onset latency, number of awakenings during the night and sleep efficiency are compared. Ten of the eleven devices measured higher total sleep time and higher sleep efficiency than the actigraph. These devices measured higher total sleep time by 1.21 % – 12.06 % and measured higher sleep efficiency by 2.86 % - 13.86 %. One device, namely Fossil Sport, measured lower total sleep time by 9.02 % and lower sleep efficiency by 9.13 %. Sleep onset latency was the most distinct parameter. Wearable devices measured higher sleep time by 86.72 % – 1225.95 %. Neither device nor actigraph could reliably determine the number of awakenings during the night unless it was a significant physical activity during the night. From the results of the work, it is not possible to say in general that all commercially available devices would be a reliable substitute for actigraphy.
|
|
|
Plasma-enhanced chemicial vapor deposition
Žák, Luboš ; Salyk, Ota (referee) ; Čech, Vladimír (advisor)
Theoretical part of diploma thesis was focused on the search of the state of knowledge in the area of plasma, plasma polymerization and characterization of thin films. Plasma-enhanced chemical vapor deposition (PECVD) was described in the experimental part together with selected analytical techniques. The technology with high level of reproducibility was reached by precise control of deposition conditions, monitoring of plasma, and analysis of plasma products using mass spectrometry. The obtained results demonstrated that the elemental composition, chemical structure, optical and mechanical properties of films were influenced by effective power used.
|
|
|
Surface analysis of xGnP/PEI nanocomposite
Červenka, Jiří ; Klapetek, Petr (referee) ; Čech, Vladimír (advisor)
Tato Diplomová práce se zabývá povrchovou analýzou nanokompozitní folie polyetherimidu (PEI) vyztuženého exfoliovanými grafitickými nanodestičkami (xGnP). Analyzovány byly take vzorky nevyztužené PEI folie a samostatné nanodestičky. Vzorky nanokompozitu a PEI folie byly plazmaticky leptány s využitím argonového plazmatu po dobu 1, 3 a 10 hod. Skenovací elektronová mikroskopie (SEM) byla použita pro charakterizaci samostatných nanodestiček rozptýlených na křemíkovém substrátu, původních či leptaných vzorků PEI folie a nanokompozitu. Nanodestičky byly identifikovány při povrchu leptané nanokompozitní folie. Mikroskopie atomárních sil (AFM) byla použita pro zobrazení povrchové topografie separovaných nanodestiček a odkrytých destiček při povrchu leptaného kompozitu. Povrchová drsnost (střední kvadratická hodnota, vzdálenost nejnižšího a nejvyššího bodu) leptaného nanokompozitu narůstala s prodlužující se dobou leptání. Akustická mikroskopie atomárních sil (AFAM) byla použita pro charakterizaci elastické anizotropie leptaných kompozitních vzorků. Nanoindentační měření umožnila charakterizaci lokálních mechanických vlastností PEI a nanokompozitních folií.
|