Cracking of ferritic stainless steel tubes during production process
Majtás, Dušan ; Kreislová, K. ; Viani, Alberto ; Pérez-Estébanez, Marta ; Geiplová, H.
From the economic reasons many products originally made from austenite stainless steel are nowadays made from ferritic stainless steel. Ferritic steels have relatively low yield strength and the work hardening is limited. They cannot be hardened by heat treatment and only moderately hardened by cold working. Commercially made stainless steel tubes from ferritic steel, used for industrial plumbing was examined on presence of cracks. The cracking was present on the inner side of the convoluted tube shape. The tube manufacturing process consisted of continual bending of the sheet to tube shape, weld the tube, then of cold shaping by pulling through rib-forming frames, which is done in several steps. Then thermal treatment applies to the nearly finished product to remove stress remaining in the structure. Prime suspect was deformation beyond the ductility of used material. However the stress-strain tensile testing does not approved this hypothesis. Several samples of failed material were taken together with reference, and were examined by optical microscopy, and X-Ray Diffraction structure analysis. The structure of the cracked tubes does not show the signs of deformation over the limit, except the location near to the crack itself. Interestingly enough the failed material showed more homogenous structure than the original one. Needle like structures were found when the material is “overetched”, on these structures concentration of stress under bending occur. This structure was identified as δ-ferrite, however its presence in α-ferrite matrix is unclear.
|
|
|
Influence of ice accretion at bridge rope on Strouhal number
Pospíšil, Stanislav ; Gorski, P. ; Kuznetsov, Sergeii
The paper is concerned with the method and results of wind tunnel investigations of the/nStrouhal number (St) of a stationary iced cable model of cable-supported bridges with/nrespect to different angles of wind attack. The methodology leading to the experimental/nicing of the inclined cable model was prepared in a climatic section of the laboratory./nThe St values were determined within the range of the Reynolds number (Re) between/n2.4·104 and 16.5·104, based on the dominant vortex shedding frequencies measured in/nthe wake of the model.
|
|
| |
|
| |
|
| |
|
|
Zjištění materiálových vlastností vzorků přírodního kamene a umělého kamene z Mariánského sloupu na Hradčanském náměstí v Praze
Slížková, Zuzana ; Zeman, Antonín ; Petráňová, Veronika ; Viani, Alberto ; Pérez-Estébanez, Marta ; Frankeová, Dita ; Ševčík, Radek ; Mácová, Petra ; Janotová, Dana ; Hasníková, Hana ; Niedoba, Krzysztof ; Hauková, Petra
V rámci průzkumu před restaurátorským zásahem byly stanoveny materiálové charakteristiky přírodních i umělých kamenů, které jsou součástí Mariánského sloupu na Hradčanském náměstí v Praze. 15 vzorků bylo podrobeno rozsáhlým instrumentálním analýzám, jejichž výstupem je nejen chemicko-mineralogické složení vzorků, ale i stupeň jejich degradace včetně popisu porézního systému a úrovně zasolení.
|
|
| |
|
| |
|
|
Výzkumná zpráva z hodnocení stavu krovu věže sv. Ducha v Telči
Bláha, Jiří ; Kloiber, Michal ; Frankl, Jiří ; Buzek, Jaroslav
Předmětem výzkumné zprávy bylo posouzení stavu a identifikace rozsahu dřevokazného poškození krovu věže sv. Ducha v Telči se zaměřením na lokalizaci kritických míst, klasifikaci stupně poškození, určení rozsahu skrytého napadení pomocí nedestruktivních přístrojů, specifikaci napadení dřeva houbami (mykologie) a hmyzem (entomologie), včetně zakreslení zjištěných výsledků do kresebné dokumentace stávajícího stavu krovu. Na základě výsledků byly navrženy konkrétní postupy pro sanační opatření a do výkresové dokumentace zakresleny prvky navržené ke konstrukční sanaci. Zpráva je založena především na přímém a zprostředkovaném (endoskopickém) vizuálním pozorování doplněném o měření pomocí přístroje pro odporové mikrovrtání.
|