Sorption Ceramic Membranes with a Functionalized Surface Layer
Zub, Yu.L. ; Tomina, V.V. ; Melnyk, I.V. ; Stolyarchuk, N.V. ; Nazarchuk, H.I. ; Sliesarenko, V.V. ; Sliesarenko, V.M. ; Topka, Pavel ; Šolcová, Olga
In the current work, we have considered and compared the deposition on the surface of ceramic membrane of the polysiloxane layers with different functional groups, such as ≡Si(CH2)3SH, ≡Si(CH2)3NH2, and ≡Si(CH2)2P(O)(OH)2, and ≡Si(CH2)3NHC(S)NHC2H5. We have also reported the fabrication of ceramic membranes with bifunctional polysiloxane surface layers, containing two types of complexing groups of different nature, or (fluoro)alkyl groups along with complexing groups. Tetraethoxysilane and bis(triethoxy)silane structuring agents were used in the study. The identification of the deposited layers on the membrane surface was carried out by IR spectroscopy. It was shown by SEM, that the functionalized layers themselves are usually formed by 50-70 nm nanoparticles and their porous structure depends on several fabrication factors.
Plný tet: SKMBT_C22014090110370 -  PDF
Plný text: content.csg - PDF
|
|
|
Samonosné pelety z (Al)-SBA-15
Topka, Pavel ; Zub, Yu.L. ; Šolcová, Olga
Samonosné pelety byly úspěšně připraveny z SBA-15 a Al-SBA-15 bez použití pojiv a plastifikátorů. U připravených samonosných pelet zůstala zachována porézní struktura původního práškového materiálu. Ve srovnání s parentním vzorkem byl pozorován pokles specifického povrchu mesopórů a jejich objemu do výše 40 % v případě pelet připravených za použití nejvyššího tlaku (17,7 MPa). Pelety Al-SBA-15 byly dostatečně mechanicky stabilní, aby si udržely strukturální integritu během vsádkové alkylace toluenu benzylalkoholem při teplotě 110 °C. Konverze dosažená s peletami Al-SBA-15 po 60 minutách reakce byla přibližně pětkrát nižší ve srovnání s práškovým Al-SBA-15.
|
|
| |
host ::
RSS.