Fatigue crack initiation and growth in 316L steel in torsional cyclic loading
 Karol, Michal ; Chlupová, Alice ; Mazánová, Veronika ; Kruml, Tomáš
Fatigue crack initiation and growth study in 316L austenitic stainless steel was made in cyclic\ntorsion. The experiments on hollow cylindrical specimens were performed at room temperature using fully reversed shear strain controlled cycles. The specimens used were polished mechanically and electrolytically to enable surface damage and crack propagation observation using optical light microscope, SEM. It was found that high density of extrusions and intrusions are formed on the specimen surface due to cyclic loading. TEM observations revealed that dislocation arrangement in well-known ladder-like structure is responsible for the localization of cyclic plastic deformation and for the origin of surface roughness in which the fatigue crack nucleate. The path of fatigue cracks leading to failure was observed, too. The crack path\nwas found to be dependent upon the applied shear strain amplitude.
Úplný záznam
Fatigue crack growth in 316L under uniaxial and torsional loading
 Karol, Michal ; Chlupová, Alice ; Mazánová, Veronika ; Kruml, Tomáš
A study of fatigue crack initiation and growth in 316L austenitic stainless steel is reported. Fatigue experiments were performed at room temperature on full cylindrical specimens cycled axially (tension-compression) and on hollow cylindrical specimens tested in reversed torsion. Microstructure and damage evolution (crack initiation and growth) on the surface of mechanically and electrolytically polished specimens were observed using light and electron microscopy. An analysis of the orientation of microcracks and macrocracks which led to failure was made. Axially loaded specimens exhibited presence of several microcracks which resulted in macrocrack propagating perpendicularly to specimen axis. In the case of torsional loading, orientation of macrocrack propagation was dependent on applied load and presence of notches. High amount of short cracks initiated parallel to specimen axis. Long cracks exhibited a tendency to bifurcate with crack branches oriented at approximately 45° to the specimen axis.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English