Nanomechanical testing of an a-C:N nanolayer prepared by ion beam assisted deposition on Ti.sub.6./sub.Al.sub.4./sub.V alloy
 Vlčák, P. ; Šepitka, J. ; Horaždovský, T. ; Jirka, Ivan ; Gregora, Ivan ; Němec, M.
We applied ion beam assisted deposition for preparing a-C:N nanolayers on Ti6Al4V alloy. A Hysitron TI 950 TriboIndenter (TM) nanomechanical test instrument was used to assess the depth profiles of the mechanical properties on modified titanium substrates. Two methods were employed : a) quasistatic partial unload, and b) dynamic Continuous Measurement of X (CMX). The average nanoindentation hardness increased from HIT similar to 5GPa for a reference sample to HIT similar to 8.6 GPa for a sample coated by an a-C nanolayer, and to HIT similar to 11.5 GPa for a sample coated by an a-C:N nanolayer. The average storage modulus of the sample coated by a-C:N increased from E' similar to 130 GPa (reference sample) to E' similar to 155 GPa. The storage modulus of the sample coated by the a-C nanolayer was less than the storage modulus of the titanium substrate.
Úplný záznam
Characterization and tribological testing of a carbon-based nanolayer prepared by ion beam assisted deposition
 Horažďovský, T. ; Kovač, J. ; Drbohlav, Ivo
Carbon-based nanolayers have been attracting much attention due to their excellent low-friction properties, their high hardness and their good wear resistance. In this work we present the results of material research aimed at reducing the friction of the functional surfaces of titanium implants, and thus extending their lifetime to reoperation. An analysis of the chemical composition showed that the modified surface is composed of a carbon-based nanolayer, a mixed interface, and a nitrogen-enriched sublayer. Raman spectroscopy showed the DLC character of the carbon-based nanolayer with sp2 rich bonds. A TiN compound was detected by X-ray diffraction in the modified surface area.\n
Úplný záznam

Viz též: podobná jména autorů
1 Horažďovský, T.
Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English