Mechanical Reinforcement of Bioglass®-Based Scaffolds
Bertolla, Luca ; Prof. Dr.-Ing. habil. Aldo R. Boccaccini (oponent) ; Kotoul, Michal (oponent) ; Pabst, Willi (oponent) ; Dlouhý, Ivo (vedoucí práce)
Bioactive glasses exhibit unique characteristics as a material for bone tissue engineering. Unfortunately, their extensive application for the repair of load-bearing bone defects is still limited by low mechanical strength and fracture toughness. The main aim of this work was two-fold: the reinforcement of brittle Bioglass®-based porous scaffolds and the production of bulk Bioglass® samples exhibiting enhanced mechanical properties. For the first task, scaffolds were coated by composite coating constituted by polyvinyl alcohol (PVA) and microfibrillated cellulose (MFC). The addition of PVA/MFC coating led to a 10 fold increase of compressive strength and a 20 fold increase of tensile strength in comparison with non-coated scaffolds. SEM observations of broken struts surfaces proved the reinforcing and toughening mechanism of the composite coating which was ascribed to crack bridging and fracture of cellulose fibrils. The mechanical properties of the coating material were investigated by tensile testing of PVA/MFC stand–alone specimens. The stirring time of the PVA/MFC solution came out as a crucial parameter in order to achieve a more homogeneous dispersion of the fibres and consequently enhanced strength and stiffness. Numerical simulation of a PVA coated Bioglass® strut revealed the infiltration depth of the coating until the crack tip as the most effective criterion for the struts strengthening. Contact angle and linear viscosity measurements of PVA/MFC solutions showed that MFC causes a reduction in contact angle and a drastic increase in viscosity, indicating that a balance between these opposing effects must be achieved. Concerning the production of bulk samples, conventional furnace and spark plasma sintering technique was used. Spark plasma sintering performed without the assistance of mechanical pressure and at heating rates ranging from 100 to 300°C /min led to a material having density close to theoretical one and fracture toughness nearly 4 times higher in comparison with conventional sintering. Fractographic analysis revealed the crack deflection as the main toughening mechanisms acting in the bulk Bioglass®. Time–dependent crack healing process was also observed. The further investigation on the non-equilibrium phases crystallized is required. All obtained results are discussed in detail and general recommendations for scaffolds with enhanced mechanical resistance are served.
|
|
|
Fracture-mechanics behaviour of ceramic foam with macroscopic stress concentrator upon the tensile test
Ševeček, O. ; Majer, Z. ; Bertolla, Luca ; Chlup, Zdeněk ; Kotoul, M.
The work investigates an influence of the macroscopic stress concentrator inside the ceramic open cell foam structure on the fracture-mechanics response of the foam upon the tensile test. As the concentrator, the central crack/rectangular notch was taken into account. The influence of the crack/notch length and width on the stress concentration ahead the concentrator tip was assessed using the simplified FE beam element based model with irregular cells simulating the real ceramic foam structure. Average principal stresses calculated on set of struts ahead the crack/notch tip were compared with average stresses in the intact structure. It was found that the ratio of these stresses increases linearly with the crack length. The stress concentration ratio is slightly lower in case of thick rectangular notch than in case of a thin crack. Furthermore, the failure load leading to complete fracture of the studied specimens, subjected to the tensile loading, were calculated using the same model. It is shown that the difference factor between the critical fracture force in case of structure without concentrator and with concentrator is very close to the concentration factor calculated from the average stresses on particular struts in the region in front of the concentrator tip.\n
|
|
|
Mechanical Reinforcement of Bioglass®-Based Scaffolds
Bertolla, Luca ; Prof. Dr.-Ing. habil. Aldo R. Boccaccini (oponent) ; Kotoul, Michal (oponent) ; Pabst, Willi (oponent) ; Dlouhý, Ivo (vedoucí práce)
Bioactive glasses exhibit unique characteristics as a material for bone tissue engineering. Unfortunately, their extensive application for the repair of load-bearing bone defects is still limited by low mechanical strength and fracture toughness. The main aim of this work was two-fold: the reinforcement of brittle Bioglass®-based porous scaffolds and the production of bulk Bioglass® samples exhibiting enhanced mechanical properties. For the first task, scaffolds were coated by composite coating constituted by polyvinyl alcohol (PVA) and microfibrillated cellulose (MFC). The addition of PVA/MFC coating led to a 10 fold increase of compressive strength and a 20 fold increase of tensile strength in comparison with non-coated scaffolds. SEM observations of broken struts surfaces proved the reinforcing and toughening mechanism of the composite coating which was ascribed to crack bridging and fracture of cellulose fibrils. The mechanical properties of the coating material were investigated by tensile testing of PVA/MFC stand–alone specimens. The stirring time of the PVA/MFC solution came out as a crucial parameter in order to achieve a more homogeneous dispersion of the fibres and consequently enhanced strength and stiffness. Numerical simulation of a PVA coated Bioglass® strut revealed the infiltration depth of the coating until the crack tip as the most effective criterion for the struts strengthening. Contact angle and linear viscosity measurements of PVA/MFC solutions showed that MFC causes a reduction in contact angle and a drastic increase in viscosity, indicating that a balance between these opposing effects must be achieved. Concerning the production of bulk samples, conventional furnace and spark plasma sintering technique was used. Spark plasma sintering performed without the assistance of mechanical pressure and at heating rates ranging from 100 to 300°C /min led to a material having density close to theoretical one and fracture toughness nearly 4 times higher in comparison with conventional sintering. Fractographic analysis revealed the crack deflection as the main toughening mechanisms acting in the bulk Bioglass®. Time–dependent crack healing process was also observed. The further investigation on the non-equilibrium phases crystallized is required. All obtained results are discussed in detail and general recommendations for scaffolds with enhanced mechanical resistance are served.
|
host ::
RSS.