ZnMg0.8Ca/Sr0.2 ternary alloys - the influence of the third element on material properties
 Čapek, Jaroslav ; Pinc, Jan ; Kubásek, J. ; Molnárová, Orsolya ; Maňák, Jan ; Drahokoupil, Jan
Zinc-based materials alloyed with the elements of the 2nd group of the periodic table have been studied as potential materials for the fabrication of various biodegradable implants. In this study, we prepared two ternary alloys: ZnMg0.8Ca0.2 (wt.%) and ZnMg0.8Sr0.2. The microstructure of both ternary alloys was similar, the main difference was in the size and morphology of the Ca/SrZn13 phase. The SrZn13 phase formed fine particles with a submicron size and had more significant hardening effect in the as-cast state compared to the CaZn13 phase. The annealing led to a transformation of the eutectic structure into the “massive” Mg2Zn11 phase which caused a significant increase of both hardness and compressive yield stress. In the annealed states, comparable hardness was observed for both alloys and higher compressive yield strength for the Ca-containing alloy.
Úplný záznam
Microstructure and mechanical properties of the potentially biodegradable ternary system Zn-Mg0. 8-Ca0.2
 Pinc, Jan ; Čapek, Jaroslav ; Kubásek, J. ; Veřtát, Petr ; Hosová, K.
Zinc and zinc alloys exhibit suitable corrosion properties for biodegradable implants. Insufficient mechanical properties (for some applications) or low biocompatible Zn2+ concentrations can be modified by the alloying by essential elements like magnesium, calcium or strontium. The alloying elements also enhance the biocompatibility of zinc due to a decrease of Zn2+ release which could be toxic in a concentration exceeding 100 µM. In this study, the microstructure and hardness of a potentially biodegradable alloy ZnMg0.8Ca0.2 were observed in relation to different cooling rates. It was found that zinc dendrites, Mg2Zn11 (MgZn2) and CaZn13 phases occur in the material structure. The micro-hardness measurements revealed constant hardness of the particular phases, however, the macro-harness slightly decreased with the decreasing cooling rate due to changes in phase sizes and distribution.
Úplný záznam

Viz též: podobná jména autorů
1 ČAPEK, Josef
4 Čapek, Jakub
26 Čapek, Jan
2 Čapek, Jan,
8 Čapek, Jiří
26 Čápek, Jan
8 Čápek, Jiří
Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English