Název: Nanomechanical testing of an a-C:N nanolayer prepared by ion beam assisted deposition on Ti.sub.6./sub.Al.sub.4./sub.V alloy
Autoři: Vlčák, P. ; Šepitka, J. ; Horaždovský, T. ; Jirka, Ivan ; Gregora, Ivan ; Němec, M.
Typ dokumentu: Příspěvky z konference
Konference/Akce: NANOCON 2015. International Conference /7./, Brno (CZ), 20151014
Rok: 2015
Jazyk: eng
Abstrakt: We applied ion beam assisted deposition for preparing a-C:N nanolayers on Ti6Al4V alloy. A Hysitron TI 950 TriboIndenter (TM) nanomechanical test instrument was used to assess the depth profiles of the mechanical properties on modified titanium substrates. Two methods were employed : a) quasistatic partial unload, and b) dynamic Continuous Measurement of X (CMX). The average nanoindentation hardness increased from HIT similar to 5GPa for a reference sample to HIT similar to 8.6 GPa for a sample coated by an a-C nanolayer, and to HIT similar to 11.5 GPa for a sample coated by an a-C:N nanolayer. The average storage modulus of the sample coated by a-C:N increased from E' similar to 130 GPa (reference sample) to E' similar to 155 GPa. The storage modulus of the sample coated by the a-C nanolayer was less than the storage modulus of the titanium substrate.
Klíčová slova: a-C:N nanolayer; carbon-based materials; hardness; ion beam assisted deposition
Zdrojový dokument: NANOCON 2015: 7th International Conference on Nanomaterials - Research and Application, Conference Proceedings, ISBN 978-80-87294-63-5

Instituce: Fyzikální ústav AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0283317

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-374057


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Fyzikální ústav
Konferenční materiály > Příspěvky z konference