Název: THE INFLUENCE OF CONSOLIDATION PROCEDURE PARAMETERS ON COMPACTION OF AL POWDER
Autoři: Lowe, T. C. ; Kunčická, L. ; Kocich, R. ; Davis, C. F. ; Hlaváč, L. ; Dvořák, Jiří
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2015 - International Conference on Metallurgy and Materials /24./, Brno (CZ), 2015-06-03 / 2015-06-05
Rok: 2015
Jazyk: eng
Abstrakt: The influence of different consolidation procedures on compaction of Al powders was evaluated. Powder preparation procedures consisted of selection of particle size distribution, cold isostatic pressing (CIP), and vacuum sintering. Processing parameters investigated included the number of compression steps, compression pressure, and sintering temperature and time. Densities of the samples after compression and also after sintering were measured and compared. The overall oxygen content was analysed using by Energy Dispersive Spectroscopy. Phase composition was determined using X-ray. Microhardness measurements were performed to evaluate the degree of compaction. Double-step CIP at 200+300 MPa and subsequent sintering at 500°C for 60 min produced the best combination of properties from all the consolidation technologies of Al particles. Of the particle size ranges studies, those with diameters between 20 and 45 μm produced the best results. Aluminum oxide was present in the structure after all the processing treatments.
Klíčová slova: Aluminum powder; cold isostatic pressing; oxygen content; sintering; X-ray
Zdrojový dokument: Metal 2015: 24th International Conference on Metallurgy and Materials, ISBN 978-80-87294-58-1

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0251700

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-200978


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
 Záznam vytvořen dne 2015-11-14, naposledy upraven 2022-09-29.


Není přiložen dokument
  • Exportovat ve formátu DC, NUŠL, RIS
  • Sdílet