Název: Thermo-mechanical and isothermal fatigue behavior of austenitic stainless steel AISI 316L
Autoři: Škorík, Viktor ; Šulák, Ivo ; Obrtlík, Karel ; Polák, Jaroslav
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2015 - International Conference on Metallurgy and Materials /24./, Brno (CZ), 2015-06-03 / 2015-06-05
Rok: 2015
Jazyk: eng
Abstrakt: Many structural components of nuclear power plant systems are made of austenitic stainless steels. These structures undergo degradation by thermo-mechanical fatigue (TMF) caused by simultaneous cyclic straining and temperature cycling, particularly during start-up, shut-down and transient operations. The present work reports the cyclic deformation behavior and fatigue damage of austenitic stainless steel AISI 316L during TMF and isothermal fatigue (IF) testing in air. Total strain controlled in-phase TMF loading in the temperature range 200 - 600 °C and isothermal fatigue (IF) at 600 °C were performed. Hardening/softening curves, cyclic stress-strain response and fatigue life diagrams were obtained both for TMF and IF tests. Fatigue damage was documented using surface relief and fracture surface observations. Mean stress evolution and fatigue degradation data are employed to discuss the fatigue behavior of 316L steel both in TMF and IF regimes.
Klíčová slova: AISI 316L; Fatigue life; In-phase cycling (IP); Isothermal fatigue (IF); Thermo-mechanical fatigue (TMF)
Číslo projektu: EE2.3.30.0063, GA15-20991S (CEP), GA13-23652S (CEP)
Poskytovatel projektu: GA MŠk, GA ČR, GA ČR
Zdrojový dokument: Metal 2015: 24th International Conference on Metallurgy and Materials, ISBN 978-80-87294-58-1

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0251589

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-200943


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference